Ultrathin tempered film and preparation process thereof

A preparation process and tempered film technology, which is applied in the direction of manufacturing tools, glass tempering, glass manufacturing equipment, etc., can solve the problems affecting the sensitivity of the touch screen, etc., and achieve the effect of enhanced anti-ultraviolet performance, good fracture resistance and light weight

Inactive Publication Date: 2020-03-27
东莞市国基光电有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned existing technical solutions have the following defects: the mobile phone tempered film in this patent is similar to the tempered film currently sold on the market. Compared with other films, it is thicker and heavier, which not only increases the weight of the mobile phone but also affects the sensitivity of the touch screen. Room for improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A preparation process for an ultra-thin tempered film, comprising the following steps:

[0034] S1. cutting: use cutting machine to cut the glass substrate into required shape and size;

[0035] S2. CNC engraving: CNC machine tools are used to carve holes corresponding to electronic product models on the glass substrate after cutting;

[0036] S3. Ultrasonic cleaning once: put the glass substrate into an ultrasonic cleaning machine for cleaning;

[0037] S4. Tempering and strengthening: the glass substrate is tempered and strengthened by physical and chemical methods;

[0038] S5. Electroplating / spraying AF: plating anti-fingerprint oil on the surface of the glass substrate;

[0039] S6. Second ultrasonic cleaning: put the glass substrate into an ultrasonic cleaning machine for second cleaning;

[0040] S7. Covering with protective film: attach protective film to both sides of the glass substrate, and pack it into storage.

[0041] Among them, the physical tempering...

Embodiment 2

[0061] A preparation process for an ultra-thin tempered film, comprising the following steps:

[0062] S1. cutting: use cutting machine to cut the glass substrate into required shape and size;

[0063] S2. CNC engraving: CNC machine tools are used to carve holes corresponding to electronic product models on the glass substrate after cutting;

[0064] S3. Ultrasonic cleaning once: put the glass substrate into an ultrasonic cleaning machine for cleaning;

[0065] S4. Tempering and strengthening: the glass substrate is tempered and strengthened by physical and chemical methods;

[0066] S5. Electroplating / spraying AF: plating anti-fingerprint oil on the surface of the glass substrate;

[0067] S6. Second ultrasonic cleaning: put the glass substrate into an ultrasonic cleaning machine for second cleaning;

[0068] S7. Covering with protective film: attach protective film to both sides of the glass substrate, and pack it into storage.

[0069] Among them, the physical tempering...

Embodiment 3

[0089] A preparation process for an ultra-thin tempered film, comprising the following steps:

[0090] S1. cutting: use cutting machine to cut the glass substrate into required shape and size;

[0091] S2. CNC engraving: CNC machine tools are used to carve holes corresponding to electronic product models on the glass substrate after cutting;

[0092] S3. Ultrasonic cleaning once: put the glass substrate into an ultrasonic cleaning machine for cleaning;

[0093] S4. Tempering and strengthening: the glass substrate is tempered and strengthened by physical and chemical methods;

[0094] S5. Electroplating / spraying AF: plating anti-fingerprint oil on the surface of the glass substrate;

[0095] S6. Second ultrasonic cleaning: put the glass substrate into an ultrasonic cleaning machine for second cleaning;

[0096] S7. Covering with protective film: attach protective film to both sides of the glass substrate, and pack it into storage.

[0097] Among them, the physical tempering...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ultrathin tempered film and a preparation process thereof. The preparation process comprises the following processes: S1, cutting: cutting a glass substrate into required shapes and sizes by adopting a cutting machine; S2, CNC fine carving: carving a hole site corresponding to the type of an electronic product in the cut glass substrate by a numerical control machine tool; S3, primary ultrasonic cleaning: putting the glass substrate into an ultrasonic cleaning machine, and cleaning; S4, tempering and strengthening: tempering and strengthening the glass substrate through a physical method and a chemical method; S5, AF electric / spray plating: carrying out electric / spray plating of anti-fingerprint oil on the surface of the glass substrate; S6, secondary ultrasoniccleaning: putting the glass substrate into an ultrasonic cleaning machine, and carrying out secondary cleaning; and S7, protective film coating: laminating protective films on two surfaces of the glass substrate, packaging and warehousing. The prepared ultrathin tempered film is light and thinner, has good toughness and shock resistance, and can be safely used for a long time.

Description

technical field [0001] The invention relates to the technical field of tempered film preparation and production, in particular to an ultra-thin tempered film and a preparation process thereof. Background technique [0002] Tempered glass film, also known as tempered glass film, is currently the most enhanced protective film for the screens of mobile phones, tablets and other electronic products. The thickness of this protective film is only 0.1mm, which can completely cover the original screen and prevent it from being damaged by external forces. , Scratch, and increase the flushing absorption, which is 5 times higher than the PET film standard, and does not affect the viewing effect of the screen. However, the current tempered film is often hard and brittle because of its texture, and the overall performance is poor in shock resistance and fragile. [0003] In response to the above problems, the Chinese patent with the patent notification number CN108046597A proposes a sho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/091C03C14/00C03C17/00C03C17/28C03C19/00C03C21/00C03B27/012B08B11/04
CPCB08B11/04C03B27/012C03C3/091C03C14/002C03C14/004C03C17/002C03C17/28C03C19/00C03C21/002C03C2214/02C03C2214/04C03C2217/78C03C2218/112
Inventor 朱竹青朱秋霖惠永杰
Owner 东莞市国基光电有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products