A kind of acceptor material based on benzimide and its preparation method and application

A technology of benzoimide and acceptor material, applied in semiconductor/solid-state device manufacturing, electric solid-state devices, semiconductor devices, etc., can solve the problems of weak absorption, narrow absorption band, wide optical band gap, etc., to increase the space Twist, reduce the optical band gap, reduce the effect of aggregation

Active Publication Date: 2021-01-26
深圳睿迅有机太阳能有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of acceptor material based on benzimide, aiming at solving the technical problems such as the narrow absorption band of ultraviolet-visible light spectrum of existing acceptor material used in organic solar cells, weak absorption, wide optical band gap, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acceptor material based on benzimide and its preparation method and application
  • A kind of acceptor material based on benzimide and its preparation method and application
  • A kind of acceptor material based on benzimide and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] The embodiment of the present invention also provides a preparation method of a benzimide-based acceptor molecule, comprising the following steps:

[0063] S10. Obtaining an aldehyde compound and an electron-withdrawing compound based on benzimide;

[0064] S20. Obtain a weakly basic catalyst, dissolve the catalyst, the aldehyde compound based on benzimide, and the electron-withdrawing compound in an organic solvent, and reflux for 12 under the condition of 60° C. to 70° C. ~24 hours, get the acceptor molecule based on benzimide;

[0065]Wherein, the aldehyde compound based on benzimide is selected from:

[0066] Compound BH or compound NH

[0067] The electron-withdrawing compound is selected from any one of the following compounds:

[0068]

[0069] Among them, R 1 , R 2 , R 3 are independently selected from C 6 ~C 30 The alkyl chain of, Y is selected from sulfur or selenium, R 4 selected from any one of hydrogen, fluorine, chlorine, cyano, methoxy, su...

Embodiment 1

[0129] A kind of preparation method of acceptor molecule BH-CN based on benzimide, as attached figure 1 The synthetic route is shown as:

[0130] S10. Compound A 1 Synthesis of aldehyde compound BH based on benzimide as starting material.

[0131] ①Compound A 1 (4.3g, 10.3mmol) was dissolved in concentrated sulfuric acid / fuming nitric acid (30mL / 75mL), refluxed at 90°C for 15 hours, then cooled to room temperature, and then gradually poured into ice water. Sodium hydroxide was added to the solution. Afterwards, the precipitate was filtered out, and then purified with a silica gel column (mobile phase: petroleum ether and dichloromethane) to obtain a white solid B 1 (3.4 g, 65.1%), MS (EI, m / z) 506.9.

[0132] ②Compound B 1 (3.4 g, 6.7 mmol) and trimethyl-(6-octylthienoselenophene)tin (11.1 g, 24.0 mmol) were dissolved in 100 mL of anhydrous toluene. Ar 2 Under protection, the Pd(PPh 3 ) 4 (0.8g, 0.69mmol) was added to the reaction solution, and stirred at reflux at...

Embodiment 2

[0140] A kind of preparation method of acceptor molecule NH-CN based on benzimide, as attached figure 2 The synthetic route is shown as:

[0141] S10. Compound A 2 Synthesis of aldehyde compound NH based on benzimide as starting material.

[0142] ①Compound A 2 (4.1g, 6.3mmol) was dissolved in concentrated sulfuric acid / fuming nitric acid (30mL / 75mL), refluxed at 90°C for 15 hours, then cooled to room temperature, and then gradually poured into ice water. Sodium hydroxide was added to the solution. Afterwards, the precipitate was filtered out, and then purified with a silica gel column (mobile phase: petroleum ether and dichloromethane) to obtain compound B as a white solid 2 (3.4 g, 4.6 mmol, 73.0%), MS (EI, m / z) 736.1.

[0143] ②Compound B 2 (3.4 g, 4.6 mmol) and trimethyl-(6-octylthienothiophene)tin (10.5 g, 22.7 mmol) were dissolved in 100 mL of anhydrous toluene. Ar 2 Under protection, the Pd(PPh 3 ) 4 (0.8g, 0.69mmol) was added to the reaction solution, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
energy conversion efficiencyaaaaaaaaaa
energy conversion efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of organic solar cells, and in particular relates to a benzimide-based acceptor material, which contains benzimide or bisbenzimide units as electron-donating units D, and is rich in cyanide The group of the group and the ketone group is used as the electron-withdrawing unit A, and the electron-withdrawing unit A is connected to both ends of the central electron-donating unit D at the same time to form a benzimide multi-ring acceptor small molecule of A-D-A conjugated structure . The acceptor material based on benzoimide of the present invention has strong light absorption in the ultraviolet-visible light region (600-1000nm), and has a narrow optical bandgap (1.07eV), which is more compatible with the existing wide-bandgap donor material energy level and high carrier mobility, and is easily soluble in common organic solvents. Applying it to organic solar cells can achieve a higher short-circuit current (12.75mA / cm 2 ) and energy conversion efficiency (5.85%), has broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of organic solar cells, and in particular relates to a benzimide-based acceptor material and a preparation method thereof, as well as the application of the acceptor material in organic solar cells. Background technique [0002] With the increasingly serious energy problems, it is imminent to develop new energy sources, and solar energy has great development prospects due to its clean, non-polluting, inexhaustible and inexhaustible advantages. How to make better use of solar energy is a key solution to the energy crisis. Organic solar cells (OPV), which use organic conjugated molecules as active materials, have many advantages such as light weight, flexibility, wide source of raw materials, low cost, solution processing and large-area preparation, and are widely accepted in the global academic and industrial circles. focus on. Among them, the photosensitive active layer material is the main material that c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D517/22H01L51/42H01L51/46
CPCC07D517/22H10K85/626H10K85/657H10K30/00Y02E10/549
Inventor 黄佳乐艮文娟史胜斌
Owner 深圳睿迅有机太阳能有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com