Preparation method of carbon nitride with two-dimensional thin-layer structure
A carbon nitride and thin-layer technology, applied in the field of material chemistry, can solve the problems of high peeling yield, pollution in the peeling process, and short time consumption, and achieve the effect of significant advantages, low cost, and short time consumption
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] A method for preparing carbon nitride with a two-dimensional thin layer structure, comprising the following steps:
[0026] Step 1: Take 1 g of melamine and dissolve melamine and glycerol phosphatidylcholine in 60 ml of deionized water according to the molar ratio of melamine and glycerol phosphatidylcholine of 1:1.38, and keep stirring for 15 minutes until it is completely dissolved to obtain a mixture solution, and then The mixture solution was placed in a polytetrafluoroethylene-lined hydrothermal kettle for hydrothermal reaction at 180°C for 10 hours, then centrifuged and washed with deionized water for 3 times, and then dried at 60°C for 12 hours to obtain a solid;
[0027] Step 2: Add 0.02g of KOH to the solid to obtain a solid mixture; then take carbon fiber according to the mass ratio of solid to carbon fiber 0.01:1 and mechanically mix it with the solid mixture as raw material, place it in a 500mL corundum crucible and cover it , and then put the crucible into ...
Embodiment 2
[0030] A method for preparing carbon nitride with a two-dimensional thin layer structure, comprising the following steps:
[0031] Step 1: Take 1 g of melamine and dissolve melamine and glycerol phosphatidylcholine in 80 ml of deionized water according to the molar ratio of melamine and glycerol phosphatidylcholine of 1:1.58, and keep stirring for 30 minutes until it is completely dissolved to obtain a mixture solution, and then The mixture solution was placed in a polytetrafluoroethylene-lined hydrothermal kettle for hydrothermal reaction at 200°C for 15 hours, then centrifuged and washed with deionized water for 4 times, and then dried at 70°C for 11 hours to obtain a solid;
[0032] Step 2: Add 0.05g of KOH to the solid to obtain a solid mixture; then take carbon fiber according to the mass ratio of solid to carbon fiber 0.018:1 and mechanically mix it with the solid mixture as a raw material, then place it in a 500mL corundum crucible and cover it , and then put the crucib...
Embodiment 3
[0037] A method for preparing carbon nitride with a two-dimensional thin layer structure, comprising the following steps:
[0038] Step 1: Take 1 g of melamine and dissolve melamine and glycerol phosphatidylcholine in 120 ml of deionized water according to the molar ratio of melamine and glycerol phosphatidylcholine of 1:2.56, and keep stirring for 60 minutes until it is completely dissolved to obtain a mixture solution, and then The mixture solution was placed in a polytetrafluoroethylene-lined hydrothermal kettle for hydrothermal reaction at 240°C for 24 hours, then centrifuged and washed with deionized water for 5 times, and then dried at 100°C for 10 hours to obtain a solid;
[0039] Step 2: Add 0.1g of KOH to the solid to obtain a solid mixture; then take carbon fiber according to the mass ratio of solid to carbon fiber 0.025:1 and mechanically mix it with the solid mixture as raw material, then place it in a 500mL corundum crucible and cover it , and then put the crucibl...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap