A kind of concrete containing coal oil coarse slag and its preparation method

A coal-to-oil and concrete technology, applied in the direction of cement production, etc., can solve the problems of high cost and complicated processing process, and achieve the effects of reduced preparation cost, reasonable compatibility and high hardness

Active Publication Date: 2022-03-04
SHEXIAN QINGZHANG CEMENT MFG CO LTD +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method is still only suitable for the treatment of coal gasification fine slag with high residual carbon content, and does not involve the treatment method of coal-to-oil coarse slag with almost no residual carbon, and the treatment process is complicated and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of concrete containing coal oil coarse slag and its preparation method
  • A kind of concrete containing coal oil coarse slag and its preparation method
  • A kind of concrete containing coal oil coarse slag and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] 1. Preparation of gelling material

[0050] (1.1) Preparation of steel slag grains and steel slag sand

[0051] Primary crushing and pre-removal of steel slag raw materials: The raw materials of converter steel slag are fed and pre-removed with a hanging iron remover. The steel slag after pre-removed iron enters the roller press for primary crushing, and then enters the vibrating screen for screening. After sieving, coarse particles I and fine particles I are produced. The particle size of the coarse particle I is 15mm, and the particle size of the fine particle I is 10mm; the coarse particle I returns to the roller press after being removed by the drum type iron remover to continue crushing, forming a closed loop; the fine particle I is separated by the powder separator, and prepared Steel slag sand and fine particle II are obtained, the particle size of the steel slag sand is 5 mm, and the particle size of the fine particle II is 2.8 mm; the fine particle II is the s...

Embodiment 2

[0070] 1. Preparation of gelling material

[0071] (1.1) Preparation of steel slag grains and steel slag sand

[0072] Primary crushing and pre-removal of steel slag raw materials: The raw material of electric furnace steel slag is fed, and pre-removed by hanging iron remover. The steel slag after pre-removed iron enters the roller press for primary crushing, and then enters the vibrating screen for screening. After sieving, coarse particles I and fine particles I are produced, the particle size of coarse particles I is 10mm, and the particle size of fine particles I is 5mm; coarse particles I return to the roller press after iron removal by the drum type iron remover to continue crushing, forming a closed loop ; After the fine particle I is selected by the powder separator, steel slag sand and fine particle II are formed. The particle size of the steel slag sand is 3mm, and the particle size of the fine particle II is 2mm; the fine particle II is the steel slag particle.

[...

Embodiment 3

[0091] 1. Preparation of gelling material

[0092] (1.1) Preparation of steel slag grains and steel slag sand

[0093] Primary crushing and pre-removal of steel slag raw materials: The raw material of electric furnace steel slag is fed, and pre-removed by hanging iron remover. The steel slag after pre-removed iron enters the roller press for primary crushing, and then enters the vibrating screen for screening. After sieving, coarse particles I and fine particles I are produced, the particle size of coarse particles I is 10mm, and the particle size of fine particles I is 5mm; coarse particles I return to the roller press after iron removal by the drum type iron remover to continue crushing, forming a closed loop ; After the fine particle I is selected by the powder separator, steel slag sand and fine particle II are formed. The particle size of the steel slag sand is 3mm, and the particle size of the fine particle II is 2mm; the fine particle II is the steel slag particle.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a concrete containing coarse slag from coal-to-oil production and a preparation method thereof. The concrete comprises the following raw materials in parts by weight: 15-20 parts of cementitious material, 30-40 parts of fine aggregate, and 40-40 parts of coarse aggregate 50 parts, 3.75-9 parts of water and 0.015-0.4 parts of water reducer; wherein, the cementitious material includes by weight parts: 3-30 parts of coal oil coarse residue, 20-60 parts of slag, 10 parts of steel slag ‑40 parts, 5‑20 parts of gypsum, 2‑15 parts of cement. The raw materials of the concrete provided by the invention have reasonable gradation and excellent mechanical properties; industrial solid wastes such as coal oil slag, slag, steel slag and gypsum are effectively utilized, and the cost is low, economical and environment-friendly. The invention also provides a corresponding preparation method, which realizes no waste, no pollution and high efficiency in the whole process.

Description

technical field [0001] The invention relates to the field of resource utilization of industrial solid waste and the technical field of building materials, in particular to a concrete containing coal-to-oil coarse residue and a preparation method thereof. Background technique [0002] my country is rich in coal reserves, but oil reserves are relatively scarce, which is far from meeting the demand for oil in my country's industrial development. The coal-to-liquids industry is a technology that uses coal as raw material to produce petrochemical products. Coarse slag and fine slag will be produced during the coal-to-oil process, and the production volume in Yulin City alone is expected to reach 10.319 million tons in 2020. At present, most of the coal-to-oil coarse residues are disposed of by stockpiling or landfilling, which not only takes up a large area of ​​land, but also easily pollutes surface water, groundwater, and soil. Stockpiling is also prone to air pollution such a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/14C04B11/30C04B7/24C04B7/147C04B7/02
CPCC04B28/14C04B28/143C04B28/144C04B28/142C04B11/30C04B7/24C04B7/147C04B7/02C04B2201/50C04B2111/00017C04B18/142C04B14/06C04B18/0427Y02P40/10
Inventor 巴浩静赵智利杨兑亨倪文杨志江杨海
Owner SHEXIAN QINGZHANG CEMENT MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com