A kind of high-efficiency protective mask based on all-fiber electret generator and preparation method thereof

A technology of electret and generator, applied in life-saving equipment, respiratory protection containers, respiratory protection devices, etc., can solve the problems affecting the filtration stability and service life of mask materials, poor wear resistance and poor flexibility of friction materials, etc. , to achieve good flexibility, ensure stability, and good air permeability

Active Publication Date: 2021-10-26
SOUTH CHINA UNIV OF TECH
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The disadvantages of the above technology are: the flexibility of metal electrode materials such as copper mesh is poor, and cracks and fractures are prone to occur in the process of continuous bending; and the friction material obtained by surface nano-modification has poor wear resistance, which directly affects Filtration stability and service life of mask materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-efficiency protective mask based on all-fiber electret generator and preparation method thereof
  • A kind of high-efficiency protective mask based on all-fiber electret generator and preparation method thereof
  • A kind of high-efficiency protective mask based on all-fiber electret generator and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A high-efficiency protective mask based on an all-fiber electret generator of the present embodiment and a preparation method thereof, the specific steps are:

[0043](1) Accurately weigh 16.2 g of N-N dimethylformamide and 10.8 g of acetone in a 50 mL beaker with an electronic balance, then weigh 0.05 g of nano-silicon dioxide (purity 99.5%, average particle size 20 nm) in In the above mixed solvent, then use an electronic balance to accurately weigh 3.0 g of polyvinylidene fluoride and place it in the above beaker, add a stirrer, and stir for 8 h with a magnetic stirrer at 60 °C, with a stirring power of 200 W, and configure it to be uniform and stable. spinning solution.

[0044] (2) Draw polyvinylidene fluoride spinning solution with a syringe, use figure 1 The electrospinning equipment shown (composed of voltage protection system 1, drum receiving control system 2, spinning solution injection system 3 and high-voltage electrostatic system 4, the same below) perfor...

Embodiment 2

[0051] A high-efficiency protective mask based on an all-fiber electret generator of the present embodiment and a preparation method thereof, the specific steps are:

[0052] (1) Accurately weigh 16.2 g of N-N dimethylformamide and 10.8 g of acetone in a 50 mL beaker with an electronic balance, then weigh 0.03 g of nano-silicon nitride (purity 99.5%, average particle size 30 nm) in In the above mixed solvent, then use an electronic balance to accurately weigh 3.6 g of polyvinylidene fluoride and place it in the above beaker, add a stirrer, and stir for 8 h at 80°C with a magnetic stirrer, with a stirring power of 300 W, and configure it to be uniform and stable. spinning solution.

[0053] (2) Draw polyvinylidene fluoride spinning solution with a syringe, use figure 1 The electrospinning equipment shown is used for electrospinning, and the non-woven fabric is used as the receiving substrate, and the electrospinning parameters are adjusted: the electrostatic high voltage is 20...

Embodiment 3

[0060] A high-efficiency protective mask based on an all-fiber electret generator of the present embodiment and a preparation method thereof, the specific steps are:

[0061] (1) Accurately weigh 30 g of dichloromethane with an electronic balance and place it in a 50 mL beaker, then weigh 0.03 g of nano-zinc oxide (average particle size 30 nm) and place it in the above solvent, and then accurately weigh 2.4 g of dichloromethane with an electronic balance. g polycarbonate was placed in the above-mentioned beaker, and ultrasonically vibrated at 60°C for 6 h with an ultrasonic power of 200 W to form a uniform and stable spinning solution.

[0062] (2) Draw the polycarbonate spinning solution with a syringe, use figure 1 The electrospinning equipment shown is used for electrospinning, and the non-woven fabric is used as the receiving substrate, and the electrospinning parameters are adjusted: the electrostatic high voltage is 25 KV, the receiving distance is 12 cm, the injection s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-efficiency protective mask based on an all-fiber electret generator and a preparation method thereof. The high-efficiency protective mask based on the full-fiber electret generator includes a tightening belt, a silicone mold, a full-fiber electret generator and a breathing valve arranged in the silicone mold. The full-fiber electret generator includes a filter layer and a sliding fixed support arranged on the filter layer; the filter layer includes successively stacked silica gel films, conductive fabrics, electret fiber membranes and non-woven fabrics; the The conductive fabric and the electret fiber membrane have different electronegativity, which can generate 200-1000V electrostatic voltage through spontaneous breathing drive. The protective mask based on full fiber electret generator of the present invention is to PM 2.5 Filtration efficiency ≥ 98%, PM 1.0 The filtration efficiency is more than 90%, the filtration pressure drop is between 20-50 Pa, and the flexibility and air permeability are good, the preparation process is simple, and it has broad application prospects in the field of personal protection.

Description

technical field [0001] The invention belongs to the technical field of personal protection and air purification, and in particular relates to a high-efficiency protective mask based on an all-fiber electret generator and a preparation method thereof. Background technique [0002] With the continuous deepening of the industrialization process, fine particulate matter has become one of the important air pollutants, causing serious harm to human health. Therefore, personal protection based on anti-smog is becoming more and more important. [0003] Traditional high-efficiency protective mask materials mainly rely on mechanical effects such as physical interception, inertial collision, and Brownian diffusion to capture fine particles. While achieving high-efficiency filtration of fine particle pollutants, the pressure resistance is also large, and the air permeability and comfort are poor. [0004] Melt-blown electret material is another widely used mask material. It introduces e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A62B7/10A62B9/02A62B23/02
CPCA62B7/10A62B9/022A62B23/02
Inventor 蔡容容雷杨张立志张昊晴
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com