A kind of recycled concrete and its preparation method

A technology of recycled concrete and recycled coarse aggregate, applied in the field of concrete, can solve the problems of poor fluidity, high water absorption rate of recycled aggregate, and low slump, so as to improve fluidity and slump, improve slump and The effect of fluidity, good resistance to deformation

Active Publication Date: 2021-12-10
西安顺通建材有限责任公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The slump of the concrete mixture prepared by the above technical scheme is low, because the waste concrete is subjected to a large external force during the crushing process, and a large number of fine cracks are prone to appear inside the aggregate, and the water absorption rate of the recycled aggregate is higher than that of the natural aggregate. Large, many pores, high surface roughness, and large amount of slurry, resulting in small slump, poor fluidity, unfavorable for construction, not easy to vibrate and compact, and the formed concrete is prone to voids and honeycombs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of recycled concrete and its preparation method
  • A kind of recycled concrete and its preparation method
  • A kind of recycled concrete and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Embodiment 1: a kind of recycled concrete, each component of its raw material and corresponding parts by weight thereof are as shown in table 1,

[0046] The glaze modified recycled coarse aggregate is prepared through the following steps:

[0047] Step 1, crushing the waste concrete into coarse aggregates of 5-25 mm in size, washing the broken coarse aggregates with water, and drying them naturally to obtain regenerated coarse aggregates;

[0048] Step 2, prepare the glaze, put the feldspar of 5±1 parts, the quartz of 5±1 parts, the calcite of 5±1 parts, the kaolin of 17±1 parts, the alumina of 4±1 parts respectively Grind in a ball mill for 20±0.5 hours, mix the ground raw materials evenly to obtain glaze;

[0049] Step 3, put the regenerated coarse aggregate into the mixing tank, add water to the glaze and stir evenly to obtain a glaze slurry, the parts by weight of the glaze, surfactant and water are 30 parts and 60 parts respectively, and add the glaze into the mi...

Embodiment 2-3

[0055] Embodiment 2-3: A kind of recycled concrete, the difference from Example 1 is that the components of its raw materials and their corresponding parts by weight are shown in Table 1, and the raw materials of the glaze slurry and their corresponding parts by weight The number is shown in Table 2, and the unit in Table 1 is kg / m 3 It is the unit of parts by weight of the raw materials required for the recycled concrete of the present invention.

[0056] Each raw material of recycled concrete and parts by weight thereof in table 1 embodiment 1-3

[0057]

[0058] components Example 1 Example 2 Example 3 glaze 30 40 38 water 60 55 55

Embodiment 4

[0059] Embodiment 4: A kind of recycled concrete, the difference from Example 1 is that in the step 3 of preparing the glaze modified recycled coarse aggregate, water and surfactant are added to the glaze, and the glaze slurry is obtained by stirring evenly. The parts by weight of surfactant is 18 parts. In this embodiment, the surfactant is sodium dodecylbenzenesulfonate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a recycled concrete and a preparation method thereof, and relates to the technical field of concrete. Its technical points are: its raw materials include the following components in parts by weight: cement 280-300 kg / m 3 ; fly ash 70‑90 kg / m 3 ; sand 800‑820 kg / m 3 ;Glaze modified recycled coarse aggregate 790‑810 kg / m 3 ;Natural gravel 190‑210 kg / m 3 ;Admixture 8‑10 kg / m 3 ; water 155‑165k kg / m 3 . The recycled concrete in the invention has the advantages of improving the slump and mechanical strength of the recycled concrete.

Description

technical field [0001] The invention relates to the technical field of concrete, more specifically, it relates to a recycled concrete and a preparation method thereof. Background technique [0002] Our country is in a period of rapid economic development. With the development of our country's economy, population growth, and urbanization of towns, the basic construction is also at a climax of development. The centralized planning of second-tier and lower cities has led to the demolition of a large number of existing buildings. The disposal of the resulting construction waste also puts a huge pressure on the environment, among which waste concrete accounts for 30%-40% of the construction waste; on the other hand, the demand for sand and gravel aggregates in Daxing construction is increasing , due to a large amount of mining, it has caused great damage to the natural environment, and the natural resources are gradually becoming exhausted. Demolition or new construction, constr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B20/10C03C8/00
CPCC04B28/04C04B20/1074C03C8/00C04B2201/50C04B18/08C04B14/06C04B18/16C04B14/02C04B2103/302C04B20/068
Inventor 刘俊涛
Owner 西安顺通建材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap