Breathable fabric and preparation method thereof

A fabric and perforated technology, applied in the field of fabric processing, can solve the problems of sunscreen clothing that cannot effectively absorb sweat and perspiration, poor wearing comfort, and inability to discharge sweat, etc., and achieves the effect of improving air permeability, reducing processing difficulty and reducing waste.

Active Publication Date: 2020-08-04
玛伊娅服饰(上海)有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the production of raincoats is mainly made of chemical fiber products with poor moisture absorption and perspiration, and the surface is coated with a layer of film. Made of high-quality chemical fibers, the surface may be coated or uncoated, because sun protection clothing is mainly worn in summer, and the sun protection clothing of this type of product cannot effectively absorb sweat and perspiration, causing people to easily suffer from heat stroke during wearing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Breathable fabric and preparation method thereof
  • Breathable fabric and preparation method thereof
  • Breathable fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0046] Such as figure 1 As shown, a breathable fabric includes a base layer 31 and a coating 32 disposed on the base layer 31, the coating material is PVDF; the base layer 31 is pure linen fabric, imitation linen fabric, cotton linen fabric or silk Hemp fabric, the base layer 31 is provided with a plurality of through holes 33; the coating 32 is coated on the base layer 31.

[0047] Due to the difficulty in achieving windproof, waterproof and breathable properties, the wearability of fabrics has always been to be improved. Therefore, a method for making breathable fabrics is provided, including:

[0048] a, prepare PVDF solution;

[0049] b. placing the PVDF solution prepared in step a on the fabric processing equipment, and simultaneously putting the base layer into the fabric processing equipment, and coating the PVDF solution on the base layer;

[0050] c. Drying the semi-finished fabric obtained in step b; the drying process is to dry the semi-finished fabric at a temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a breathable fabric. The breathable fabric comprises a base layer and a coating layer arranged on the base layer, wherein the coating layer is made of PVDF; the base layer is apure linen fabric, a simulated linen fabric, a cotton linen fabric or a silk linen fabric, and a plurality of through holes are formed in the base layer; and the base layer is coated with the coatinglayer. A preparation method of the breathable fabric comprises the following steps of a, preparing a PVDF solution; b, putting the PVDF solution prepared in the step a into fabric processing equipment, simultaneously putting the base layer into the fabric processing equipment, and coating the base layer with the PVDF solution; and c, drying the semi-finished fabric obtained in the step b, specifically, drying the semi-finished fabric at the temperature condition of 120-150 DEG C to obtain the above fabric. The multiple through holes are formed in the base layer, so that the ventilation performance of clothes is improved, the influence of the PVDF layer on the ventilation performance of the base layer is reduced, and the wearing comfort of the fabric is improved.

Description

technical field [0001] The invention belongs to the technical field of fabric processing, and in particular relates to a breathable fabric and a preparation method thereof. Background technique [0002] Coating technology is widely used in all walks of life. In the international textile industry, coated products account for more than 25% of all textile products. Coated fabrics have functions such as water repellency, windproof, flame retardant, antifouling, shading, and radiation protection. And have the appearance of imitation leather or present a pleasing gloss. [0003] At present, the production of raincoats is mainly made of chemical fiber products with poor moisture absorption and perspiration properties, and the surface is coated with a layer of film, which will easily cause sweat to not drain out of the body after wearing, and the wearing comfort is poor; sun protection clothing mainly uses high-density high-density Made of high-quality chemical fibers, the surface ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N3/00D06N3/04B26F1/24
CPCD06N3/047D06N3/0002D06N3/0015D06N3/0077D06N3/0088B26F1/24D06N2209/123D06N2209/128D06N2211/10B26F2210/12
Inventor 金志远
Owner 玛伊娅服饰(上海)有限公司