Ultra-high-strength hot-rolled steel sheet, steel pipe, member, and manufacturing methods therefor

A hot-rolled steel plate, ultra-high-strength technology, applied in the direction of manufacturing tools, heat treatment furnaces, heat treatment equipment, etc., can solve the problems that have not been raised, and achieve the effect of inhibiting permeation and excellent hydrogen permeation resistance

Active Publication Date: 2020-08-07
浦项股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, Patent Document 2 proposes that by introducing a ferrite phase into the final microstructure, elongation at the level of 15% and tensile strength at the level of 900-1200 MPa can be ensured, so it is judged that in securing a similar level of elongation At the same time, there are limitations in ensuring ultra-high strength above 1800MPa
[0005] Therefore, according to the analysis of the manufacturing process of the steel plate and steel member proposed in the above-mentioned patent documents, it is not proposed that the steel plate or member has a tensile strength of 1800 MPa or more and a tensile strength of 20000 MPa% or more through quenching-tempering heat treatment A hot-rolled steel sheet, a hot-rolled pickled steel sheet, a steel pipe, and a method for producing the same having a value of × elongation and excellent resistance to hydrogen permeation from the outside such as a corrosive environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-high-strength hot-rolled steel sheet, steel pipe, member, and manufacturing methods therefor
  • Ultra-high-strength hot-rolled steel sheet, steel pipe, member, and manufacturing methods therefor
  • Ultra-high-strength hot-rolled steel sheet, steel pipe, member, and manufacturing methods therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0183] Hereinafter, the present invention will be described in more detail through examples.

[0184] (Example)

[0185]Using the steels with the compositions in Table 1 and Table 2 below, hot rolling was carried out under the conditions in Table 3 below to produce hot-rolled steel sheets with a thickness of 3 mm, which were then pickled. Before hot rolling, the manufactured slabs are heated for 200 minutes at a temperature range of 1200±20°C for homogenization, and then each slab is subjected to rough rolling and finish rolling at a temperature of 600-700°C Coiled to obtain a hot-rolled steel plate with a thickness of 3 mm.

[0186] In Table 1 and Table 2 below, Invention Steels (1 to 5) satisfy Relational Expression (1) and Relational Expression (2), and the sum of Cu+Ni is 1.1 or more. Comparative steel (1) does not satisfy relational expression (1) and relational expression (2), and the sum of Cu+Ni is less than 1.1, and the sum of Cu+Ni of comparative steel (2) is less ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A preferable aspect of the present invention provides: an ultra-high-strength hot-rolled steel sheet containing, by weight, one or two of 0.40-0.60% of C, 0.7-1.5% of Mn, 0.3% or less (excluding 0%) of Si, 0.03% or less (including 0%) of P, 0.004% or less (including 0%) of S, 0.04% or less (excluding 0%) of Al, 0.3% or less (excluding 0%) of Cr, 0.3% or less (excluding 0%) of Mo, 0.9-1.5% of Ni, and 0.9-1.5% of Cu, 1.1% or more of Cu+Ni, 0.04% or less (excluding 0%) of Ti, 0.005% or less (excluding 0%) of B, 0.006% or less (excluding 0%) of N, and the balance Fe and other impurities, the alloyelements satisfying relational formulas 1 and 2 below, wherein a microstructure of the hot-rolled steel sheet comprises, by volume, 7% or more of ferrite and 93% or less of perlite; a steel pipe anda member each using the same; and manufacturing methods therefor. [Relational formula 1] (Mn / Si) >= 3 (weight ratio) [Relational formula 2] (Ni / Si) >= 1 (weight ratio)

Description

technical field [0001] The present invention relates to a high-strength hot-rolled steel sheet used for automotive component materials, etc., steel pipes and parts using the hot-rolled steel sheet, and their manufacturing methods, and more specifically, to an ultra-high-strength hot-rolled steel sheet, Steel pipes and components of rolled steel sheets having a value of tensile strength×elongation of 20,000 MPa% or more, excellent in resistance to external hydrogen permeation, and exhibiting ultrahigh strength after heat treatment, and their manufacturing methods. Background technique [0002] In order to meet the strengthening of automobile collision safety regulations and the improvement of fuel efficiency, the weight reduction and high strength of automobile components are continuously being carried out. In general, ductility or elongation tends to decrease when the strength of automotive component materials is increased. In addition, in order to simultaneously secure str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/44C22C38/54C22C38/04C21D8/02C21D9/46C23G1/08C22C38/42C22C38/50C22C38/02
CPCC21D9/46C22C38/02C22C38/04C22C38/42C22C38/44C22C38/50C22C38/54C23G1/08C22C38/06C22C38/001C21D2211/005C21D2211/009C21D9/48C21D9/08C21D8/105C21D8/0463C21D8/0263C21D8/0226C21D8/0426C21D6/004C21D6/005C21D6/008C21D1/26C21D1/18C21D1/185B23K2103/04B23K9/0253B23K11/0935Y02P10/20C21D2211/008C21D9/085C21D2211/001C22C38/002C22C38/105C22C38/12C22C38/28C22C38/32C23G1/00
Inventor 成焕球赵悦来裵成范
Owner 浦项股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products