A high-performance powder steel thermal spray deposition molding process

A technique for deposition-molded, powdered steel

Active Publication Date: 2022-06-03
北京赛亿科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Spray deposition technology is used to prepare metal matrix composite ingots. In the current research and practice, most of the intubation method is used to directly spray the reinforced solid phase particles into the metal melt atomization cone, but this method is not easy to ensure the solid phase Uniform distribution of particles in the deposited body with low material utilization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-performance powder steel thermal spray deposition molding process
  • A high-performance powder steel thermal spray deposition molding process
  • A high-performance powder steel thermal spray deposition molding process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Example 1: see Figure 1-4, 1. A high-performance powder steel thermal spray deposition molding process, the molding process is:

[0039] S1, the technician controls the stopper rod 2 to descend, so that part of the molten metal in the molten metal tank 1 is injected into the mixing chamber 3 through the liquid guide block 5. The molten metal is elemental metal liquid or alloy liquid; the metal powder is aluminum oxide or iron oxide, etc. Magnetizable metal oxide;

[0040] S2, at the same time, the solid input pipe 4 introduces the magnetized metal powder in the metal powder storage tank into the mixing chamber 3 through the solid input pipe 4, so that the magnetized metal powder is mixed with the liquid metal;

[0041] S3, open the compressed gas valve, the atomizer 7 starts to work, the compressed gas injected into the atomizer 7 is inert gas such as nitrogen, argon or helium, and the inert gas shielding gas is introduced to protect the atomized metal liquid and prev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance powder steel thermal spray deposition molding process, which belongs to the field of powder steel manufacturing technology. It is a high-performance powder steel thermal spray deposition molding process. The liquid block is injected into the mixing chamber, and the solid input pipe introduces the metal powder into the mixing chamber, so that the magnetized metal powder is mixed with the liquid metal. The filter plate guides the flow, so that the metal powder and part of the atomized metal liquid enter the inner guide column, and the other part of the atomized metal liquid flows through the outer guide column, so that the outer layer sprayed out of the guide tube is the atomized metal liquid. The inner layer is a double-layer jet fluid of a mixture of metal powder and atomized metal liquid, which can realize the spray deposition of powder steel through the double-layer jet fluid. The solid particles are evenly distributed.

Description

technical field [0001] The invention relates to the field of powder steel manufacturing process, more particularly, to a high-performance powder steel thermal spray deposition molding process. Background technique [0002] The principle of jet deposition technology is: the molten metal flowing out of the flow pipe is broken by the high-speed air flow at the atomization spray outlet, and atomized into a fine and dispersed droplet jet. The air flow conducts heat exchange. Among them, the droplets smaller than a certain critical size solidify into solid particles, the larger size droplets are still liquid, and the intermediate size droplets are semi-solidified particles containing a certain proportion of liquid phase. These solidification degrees are different After the molten droplets hit the deposition surface at high speed, they attach, spread, accumulate and fuse with the surface to form a thin semi-liquid layer, and then solidify and crystallize sequentially, gradually dep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C4/123C23C4/06
CPCC23C4/123C23C4/06Y02P10/25
Inventor 陈辉
Owner 北京赛亿科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com