Super-hydrophobic paint with super-strong mechanical properties and preparation method thereof

A technology with mechanical properties and super-hydrophobicity, applied in coatings, epoxy resin coatings, polyether coatings, etc., can solve the problems of weak mechanical properties, difficult to prepare the surface of various substrates, etc. Wetting-response properties, the effect of increasing the range of applications

Inactive Publication Date: 2020-09-04
CHINA UNIV OF GEOSCIENCES (WUHAN)
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the present invention provides a super-hydrophobic paint with super-strong mechanical properties and a preparation method thereof, which solves the technical problems that responsive super-wetting materials generally have weak mechanical properties and are difficult to prepare on the surface of various substrates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-hydrophobic paint with super-strong mechanical properties and preparation method thereof
  • Super-hydrophobic paint with super-strong mechanical properties and preparation method thereof
  • Super-hydrophobic paint with super-strong mechanical properties and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] refer to figure 1 , the present invention also provides the preparation method of the superhydrophobic paint of above-mentioned super strong mechanical property, comprises the following steps:

[0029] Step S1, weighing 1-10 parts of epoxy resin and 0.4-2.4 parts of polyethylene glycol in parts by mass, mixing them, adding absolute ethanol, and magnetically stirring;

[0030] Step S2, adding absolute ethanol to 1 to 2.5 parts of titanium dioxide in parts by mass, and magnetically stirring;

[0031] Step S3, mixing the solution of step S1 and the solution of step S2, adding 1.6-5 parts of 1H,1H,2H,2H-perfluorooctyltriethoxysilane, 0.02-0.12 parts of poly( N-isopropylacrylamide), 0.1-1.2 parts of fluorosilane, 0.2-1.2 parts of curing agent, magnetic stirring, and ultrasonic treatment to obtain super-hydrophobic paint.

Embodiment 1

[0034] In a 100mL beaker, add 5g of epoxy resin and 2.0g of polyethylene glycol, then add 30mL of absolute ethanol solution, then stir in a magnetic stirrer for 15min; weigh 1.5g of titanium dioxide particles (P25 titanium dioxide and 200nm anatase The mass ratio of ore titanium dioxide is 2.0:1) into a 250mL blue-necked bottle, then add 70mL of absolute ethanol solution, and then magnetically stir for 15min; mix the epoxy resin and titanium dioxide solution, then add 3.5g1H, 1H, 2H,2H-Perfluorooctyltriethoxysilane, magnetically stirred for 15min, ultrasonically treated for 15min, repeated stirring and ultrasonically for 2 times; then added 0.1g poly(N-isopropylacrylamide), stirred and ultrasonically treated for 5min each ; Finally, add 0.6g fluorosilane and 0.8g ethylenediamine, stir magnetically for 5min, ultrasonicate for 10min, and stir magnetically for 5min again to obtain a superhydrophobic paint.

[0035] In Example 1, every 1 g is one serving.

[0036] The paint prepa...

Embodiment 2

[0042] In a 100mL beaker, add 8g of epoxy resin and 0.6g of polyethylene glycol, then add 30mL of absolute ethanol solution, and then stir in a magnetic stirrer for 15min; weigh 2.0g of titanium dioxide particles (P25 titanium dioxide and 200nm anatase The mass ratio of ore titanium dioxide is 1:1) into a 250mL blue bottle, then add 70mL of absolute ethanol solution, and then magnetically stir for 15min; mix the epoxy resin and titanium dioxide solution, then add 2.0g1H, 1H, 2H,2H-Perfluorooctyltriethoxysilane, magnetic stirring for 15min, ultrasonic treatment for 15min, stirring and ultrasonic treatment repeated twice; then add 0.05g poly(N-isopropylacrylamide), stirring and ultrasonic treatment for 5min each ;Finally, add 0.5g fluorosilane and 1.0g hexamethylenediamine, stir magnetically for 5min, treat with ultrasonic for 10min, and stir magnetically again for 5min to obtain the superhydrophobic paint.

[0043] In Example 2, every 1 g is one serving.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
contact angleaaaaaaaaaa
Login to View More

Abstract

The invention provides a super-hydrophobic paint with super-strong mechanical properties. The material is prepared from the following raw materials in parts by mass. The paint is prepared from the following components in parts by weight: 1 to 10 parts of epoxy resin, 0.4 to 2.4 parts of polyethylene glycol, 1 to 2.5 parts of titanium dioxide, 1.6 to 5 parts of 1H, 1H, 2H, 2H-perfluorooctyltriethoxysilane, 0.02 to 0.12 part of poly (N-isopropylacrylamide), 0.1 to 1.2 parts of fluorosilane and 0.2 to 1.2 parts of curing agent. The invention also provides a preparation method of the super-hydrophobic paint. The super-hydrophobic paint provided by the invention solves the technical problems that a responsive super-wetting material is generally weak in mechanical property and is not easy to prepare on the surfaces of various base materials.

Description

technical field [0001] The invention relates to the field of preparation and application of superwetting responsive materials, in particular to a superhydrophobic paint with super strong mechanical properties and a preparation method thereof. Background technique [0002] The wettability of materials is judged by the surface water contact angle (WCA), which can be divided into four types, namely superhydrophilic, hydrophilic, hydrophobic, and superhydrophobic. When WCA<10°, the surface is called superhydrophilic material; when 10°<WCA<90°, the surface is hydrophilic material; when 90°<WCA<150°, the surface is hydrophobic material; when When WCA>150°, the surface is a superhydrophobic material. The main method of preparing special wettability materials is to construct the microstructure and modify the chemical composition of the surface. [0003] The research on wettability materials mainly focuses on responsive wettability materials. When there are exter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D171/02C09D133/24C09D7/62C09D7/63
CPCC08K2003/2241C08K2201/003C08K2201/011C08K2201/014C08L2205/03C09D163/00C09D7/62C09D7/63C08L71/02C08L33/24C08K9/06C08K5/5419C08K3/22
Inventor 夏帆朱海
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com