Power storage battery plastic shell corrosion resistance testing device and method

A technology of power battery and testing device, applied in the direction of measuring device, lead-acid battery, testing material hardness, etc., can solve the problems of easy corrosion of battery shell, leakage of oily substances, cracking, etc., to avoid batch quality problems, The effect of the convenience of the test method

Active Publication Date: 2020-09-25
ZHEJIANG TIANNENG BATTERY JIANGSU +3
View PDF14 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a power storage battery plastic casing corrosion resistance testing device and its method, which overcomes the defects of the prior art and solves the problem of rubber pads made of recycled rubber, which will ooze oily substances, making the battery casing prone to corrosion and cracking quality problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Power storage battery plastic shell corrosion resistance testing device and method
  • Power storage battery plastic shell corrosion resistance testing device and method
  • Power storage battery plastic shell corrosion resistance testing device and method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: as figure 1 , figure 2 The shown one kind of test device for corrosion resistance of the molded case of power storage battery includes a middle cover 1 and a pressing device 2. The pressing device 2 includes a fixing frame 21, a horizontal pallet 22, and a locking device 23. The fixing The frame 21 is U-shaped and the U-shaped opening faces to the left. The left end of the bottom plate is integrally connected with a vertical support rod 24. The top of the support rod 24 is welded with a horizontal pallet 22 on which a middle Cover 1; the left end of the top plate of the fixing frame 21 is provided with a locking device 23, and the locking device 23 fixes the rubber pad 3 at the center of the top surface of the middle cover 1; the locking device 23 includes locking bolts 25. Pressing plate 26, limit nut A27, limit nut B28, the screw rod of the locking bolt 25 runs through the top plate of the fixing frame 21 from top to bottom and is connected with the pr...

Embodiment 2

[0039] 1. Cut out a square rubber pad with a side length of 25mm, and place it on the top surface of the middle cover;

[0040] 2. Place the pressure plate on the top surface of the rubber pad, and use the torque wrench to tighten the locking bolt. When the locking bolt presses the pressure plate, the torque value of the control torque wrench is: 20Nm;

[0041] 3. The whole device is placed in a high and low temperature box, the temperature is set at 60°C, and the time is 60h;

[0042]4. After the time is over, take out the whole device, let it cool down to room temperature 25°C, and take out the rubber pad, observe the change of the surface color of the rubber pad and compare the average hardness values ​​X1, X2, X3, X4, X5, X6, X7, The difference Y between X8, X9 and X (set the value of X to be 81):

[0043]

[0044] In terms of color change, the area of ​​S1 turns yellow, and it is preliminarily judged that it has been corroded; and according to the comparison of the da...

Embodiment 3

[0047] 1. Cut out a square rubber pad with a side length of 25mm, and place it on the top surface of the middle cover;

[0048] 2. Place the pressure plate on the top surface of the rubber pad, and use the torque wrench to twist the locking bolt. When the locking bolt presses the pressure plate, the torque value of the torque wrench is controlled to 20Nm;

[0049] 3. The whole device is placed in a high and low temperature box, the temperature is set at 60°C, and the time is 60h;

[0050] 4. After the time is over, take out the whole device, let it cool down to room temperature 25°C, and take out the rubber pad, observe the change of the surface color of the rubber pad and compare the average hardness values ​​X1, X2, X3, X4, X5, X6, X7, The difference Y between X8, X9 and X (set the value of X to be 81):

[0051]

[0052] In terms of color change, there is no obvious change in the S1 area, and it is preliminarily judged that it has not been corroded; and according to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a power storage battery plastic shell corrosion resistance testing device and method. The device comprises a middle cover and further comprises a pressing device, the pressingdevice comprises a fixing frame, a horizontal supporting table and a locking device, the fixing frame is in a U shape, a U-shaped opening of the fixing frame faces leftwards, a vertical supporting rodis integrally connected to the end of the left side of a bottom plate of the fixing frame, the horizontal supporting table is welded to the top of the supporting rod, and the middle cover is placed on the horizontal supporting table. The locking device is arranged at the end of the left side of a top plate of the fixing frame and fixes a rubber mat to the top face of the middle cover. It is knownfrom the structure of the invention that the test method is convenient and fast. The rubber mat is promoted to rapidly release oil substances through a high-pressure and high-temperature technology,and whether the rubber mat corrodes the middle cover or not is rapidly judged by observing the color change of the rubber mat and comparing the hardness test data of the middle cover in a rubber mat coverage area with the hardness test data of other areas of the middle cover, so that the batch quality problem of products is avoided.

Description

technical field [0001] The invention relates to the field of storage battery testing, in particular to a device for testing the corrosion resistance of a molded casing of a power storage battery and a method thereof. Background technique [0002] Lead-acid batteries have mature technology, low cost, and excellent performance. They are widely used in many application fields and become the power source of choice for the public. As one of the parts of the lead-acid battery, the battery case is used to carry the pole group, electrolyte, etc. The battery case is often made of ABS, which is cheap, has good acid and alkali resistance, high strength and good processing sex. [0003] However, the ABS material is sensitive to engine oils. Once the surface of the battery case is stained with organic oils, it is easy to cause corrosion and cracks. At present, the entire manufacturer installs rubber pads on the battery brackets of electric vehicles to cushion, and some manufacturers us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G01N17/00G01N3/40H01M2/10H01M10/06
CPCG01N3/40G01N17/00G01N17/002G01N2203/0076H01M10/06Y02E60/10
Inventor 李军陈战营孙磊胡国柱
Owner ZHEJIANG TIANNENG BATTERY JIANGSU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com