A method for improving the indentation defects of high-quality aluminum alloy round ingot soaking heat treatment

A technology of soaking heat treatment and aluminum alloy, which is applied in the field of aluminum alloy heat treatment, and can solve problems such as oxidation inclusions, plastic deformation of extrusion products, extrusion equipment extrusion cylinder, extrusion mold damage, etc.

Active Publication Date: 2021-12-28
FUJIAN NANPING ALUMINUM
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the thermal expansion of the aluminum alloy round ingot and the rack under the high temperature in the soaking furnace, the friction coefficient between aluminum and steel is different, which makes the relative movement of the contact between the round ingot and the soaking rack, resulting in deformation, resulting in round The indentation defects of pits appear at the contact position between the ingot and the soaking rack, especially the high-quality low-strength alloy ingots have low hardness, and the plastic deformation is particularly obvious. Aluminum alloy round bars with such defects are extruded , not only will cause damage to the extrusion cylinder and extrusion die of the extrusion equipment, but also easily form quality defects such as oxidation inclusions and pores in the extrusion products, causing huge losses to the manufacture of precision high-quality aluminum alloy extrusions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1 of the present invention is: a method for improving indentation defects in soaking treatment of high-quality aluminum alloy round ingots, which specifically includes the following steps:

[0027] S1: Place the aluminum alloy round ingot on an aluminum alloy plate with a thickness greater than 5mm; fix the aluminum alloy plate horizontally on the work frame through bolts;

[0028] S2: Preheating the aluminum alloy round ingot, the preheating temperature is 475°C, and the preheating time is 4h;

[0029] S3: Perform homogenization treatment on the aluminum alloy round ingot, the homogenization temperature is 550° C., and the homogenization time is 3 hours.

[0030] The difference between the second embodiment of the present invention and the first embodiment is that: the preheating temperature is 500°C, the preheating time is 5 hours; the homogenization temperature is 575°C, and the homogenization time is 5 hours.

[0031] The difference between Embodiment 3 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to the technical field of heat treatment of aluminum alloys, and in particular to a method for improving indentation defects in soaking heat treatment of high-quality aluminum alloy round ingots, which specifically includes the following steps: S1: placing aluminum alloy round ingots on an aluminum Alloy plate; S2: Preheat the aluminum alloy round ingot, the preheating temperature range is 475-525°C, and the preheating time is 4-7h; S3: Homogenize the aluminum alloy round ingot, the homogenization temperature The range is 550~600℃, and the homogenization time is 3~10h. The method for improving the indentation defect of the high-quality aluminum alloy round ingot soaking treatment provided by the invention eliminates the indentation defect on the surface of the round ingot, improves the mechanical properties of the round ingot, and improves the quality of aluminum alloy products.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy heat treatment, in particular to a method for improving indentation defects of high-quality aluminum alloy round ingot soaking heat treatment. Background technique [0002] Aluminum alloy has the characteristics of light weight, good formability, high strength, corrosion resistance, and recyclability. It has been widely used in architectural decoration, machinery, IT electronics and other fields. With the development of modern industry and technology, aluminum alloy products are widely used in aerospace The application in fields such as , ships, rail transit, and automobile lightweight is expanding year by year, which puts forward higher requirements for the comprehensive quality of aluminum alloy materials. [0003] Aluminum alloy products are processed from billets by plastic processing methods, such as extrusion, rolling, forging, etc. Among them, billets commonly used for extrusion are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/04
CPCC22F1/04
Inventor 周策路宝坤郭昆闵爱武吴洪胜余国栋李广华
Owner FUJIAN NANPING ALUMINUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products