A TC-50, oil pipe technology, applied in the direction of manufacturing converters, workpiece heating devices, manufacturing tools, etc., can solve the problem of cost of adding Ca, and achieve the effects of low cost, high yield strength, and high tensile strength

Active Publication Date: 2021-12-14
YANAN JIASHENG PETROLEUM MACHINERY
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although achieved 200J / cm at 0°C 2 Level of lateral impact value, but need to add Ca as cost, and 200J / cm 2 It has far exceeded the technical requirements. For the general formation structure, it is not necessary to spend the cost of Ca addition to increase the lateral impact value to such a high level as 200J / cm2

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A rare earth-containing tc-50 steel grade petroleum tube blank
  • A rare earth-containing tc-50 steel grade petroleum tube blank

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0026] Those skilled in the art understand that in steel products of various steel grades, some chemical components are usually added to improve various properties of the steel.

[0027]Such as carbon (C), as the carbon content in steel increases, its yield point and tensile strength increase, and its cold brittleness increases. At the same time, its plasticity and impact property decrease, and its weldability becomes poor.

[0028] Such as silicon (S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a rare earth-containing TC-50 steel grade petroleum pipe blank, which is composed of the following chemical components in mass percentage: C 0.28-0.32%; Si 0.15-0.30%; Mn 1.45-1.60%; P≤0.018%; S≤0.008%; Cr 0.15‑0.25%; Al 0.015‑0.040%; Ce 0.0005‑0.0020%; Ni<0.10%; Cu<0.10%; the balance is Fe and impurities. A kind of production method of TC-50 steel grade oil pipe blank containing rare earth, produces a kind of TC-50 steel grade petroleum pipe blank containing rare earth, a kind of TC-50 steel grade oil casing pipe containing rare earth, uses a kind of Made of rare earth TC‑50 steel grade petroleum pipe blanks. The invention discloses a production method of a rare earth-containing TC-50 steel grade oil casing, and produces a rare earth-containing TC-50 steel grade oil casing. The beneficial effects of the invention are: high tensile strength, high yield strength and high transverse impact resistance.

Description

technical field [0001] The invention relates to the production of oil casing pipes, in particular to a rare earth-containing TC-50 steel grade oil pipe blank. Background technique [0002] TC-50 steel grade oil casing is a high value-added product, usually used for medium-depth oil and gas wells of about 3000 meters, and can also be used for heavy oil thermal recovery wells of about 2000 meters, mainly as technical casing and surface casing use. With the continuous increase of oil and gas drilling and production in various countries in the world, the J55 steel grade oil casing cannot meet the drilling and production needs, and the N80 steel grade oil casing has the disadvantage of high cost and is not economical. [0003] For example, a kind of 80ksi steel grade straight seam welded oil casing steel disclosed in Chinese patent CN101376943A uses C, Si, Mn, Al, excess Fe and other components to obtain a coil with a yield strength of 600-645MPa through a straight seam welding ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/42C22C38/58B21B19/04B21B45/00B21C37/06B21D3/00C21C5/35C21C7/10
CPCC22C38/02C22C38/04C22C38/002C22C38/06C22C38/005C22C38/42C22C38/58C21C7/0006C21C7/10C21C5/35B21B45/004B21B19/04B21D3/00B21C37/06
Inventor 苏忠贵苏小东黄岩岗刘文红秦进李亮
Owner YANAN JIASHENG PETROLEUM MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products