Medium-high carbon steel hot-rolled wire rod and production method thereof

A hot-rolled wire rod and production method technology, applied in metal rolling, metal rolling, manufacturing tools, etc., can solve problems such as environmental pollution, and achieve the effects of improving production efficiency, excellent peeling effect, and excellent structure and performance.

Active Publication Date: 2020-11-03
INST OF RES OF IRON & STEEL JIANGSU PROVINCE +2
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the pickling removal method will produce a large amount of waste acid and waste gas, causing environmental pollution, therefore, in production, it is more and more inclined to abandon the pickling method and use more environmentally friendly mechanical peeling methods to remove wire rods Iron oxide scale on the surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medium-high carbon steel hot-rolled wire rod and production method thereof
  • Medium-high carbon steel hot-rolled wire rod and production method thereof
  • Medium-high carbon steel hot-rolled wire rod and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0042] One embodiment of the present invention provides a production method for hot-rolled medium-high carbon steel wire rod. In the production method, the billet is prepared into a wire rod through a heating process, a hot rolling process and a Stelmore cooling process in sequence. Moreover, an embodiment also provides a wire rod prepared based on the production method.

[0043] Wherein, the carbon content of the billet is ≥0.45% by weight, and correspondingly, the prepared wire rod also has a carbon content of ≥0.45% by weight, that is, the production method involves Production and preparation of medium and high carbon steel hot-rolled wire rods with carbon content ≥ 0.45%. Next, the heating process, the hot rolling process, and the Stelmore cooling process of a preferred embodiment of the present invention will be sequentially introduced.

[0044] (1) Heating process

[0045] The billet is heated in a heating furnace, and in this heating process, the soaking section tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a medium-high carbon steel hot-rolled wire rod and a production method thereof. According to the production method, a blank is prepared into the wire rod through heating, hot rolling and stelmor cooling, the carbon content of the blank is larger than or equal to 0.45%, and the soaking section temperature of the heating procedure ranges from 1,140 DEG C to 1,250 DEG C; the hot rolling procedure comprises rough rolling, intermediate rolling, pre-finish rolling, finish rolling and spinning in sequence, and the initial rolling temperature is 1,030-1,100 DEG C; the spinningtemperature is 900-950 DEG C; the hot rolling procedure further comprises water cooling before finish rolling with the water flow being 1,200-1,800 L / min and 400-600 L / min in sequence, water cooling in finish rolling with the water flow being 20-100 L / min and the water pressure being 0-0.3 bar, and water cooling after finish rolling with the water flow being 1,200-1,800 L / min, 400-600 L / min and 900-1,200 L / min in sequence; and in the Stelmor cooling procedure, the speed of a roller way at an inlet section is 0.6-0.8 m / s, the first one or two fans and heat preservation covers are stopped, the continuous 6-13 fans and heat preservation covers behinds are started, all the fans and heat preservation covers behinds are stopped, and the air volume of the started fans is 50-100%. The obtained wire rod is excellent in structure and performance, the surface oxide scale is controlled, the bubble problem is avoided, and the wire rod is suitable for mechanical husking.

Description

technical field [0001] The invention belongs to the technical field of steel production and manufacturing, and specifically relates to a production method of medium-high carbon steel hot-rolled wire rod, especially a production method of medium-high carbon steel hot-rolled wire rod suitable for mechanical peeling, and also relates to a production method based on A medium-high carbon steel hot-rolled wire rod prepared by the production method. Background technique [0002] Various steel wire products produced from wire rods are widely used in many aspects of society, such as automobiles, communication cables, bridges, construction machinery and other fields. Therefore, the performance requirements of wire rods are very strict. It determines the quality of steel wire products. [0003] Usually the wire rod is rolled at high temperature, and the surface of the wire rod will inevitably form a certain thickness of iron oxide scale. Before further drawing and other deep processi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B21B1/16B21B45/02B21B37/74
CPCB21B1/16B21B45/0203B21B37/74
Inventor 沈奎于学森张宇麻晗
Owner INST OF RES OF IRON & STEEL JIANGSU PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products