Low-temperature-resistant PC alloy material and preparation method thereof

An alloy material, low temperature resistance technology, applied in the field of engineering plastics, can solve the problems of reducing material toughness or low temperature resistance, limiting the use range of materials, affecting the flame retardant performance of resin, etc., to improve toughness and low temperature toughness, reduce interface voiding , Improve the effect of solvent resistance

Pending Publication Date: 2021-02-05
TIANJIN KINGFA NEW MATERIAL
View PDF11 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When applied to home appliances, electrical appliances or industrial machine shells, the material usually needs to meet the flame retardant requirements of V-0. In addition, when used outdoors, the material requires high toughness and low temperature resistance. Conventional PC or PBT flame retardants will Significantly reduce the toughness or low temperature resistance of the material, limiting the scope of use of the material
In order to make up for the damage of the flame retardant to the toughness of the resin, a toughening agent is usually added to improve the toughness, while the commonly used toughening agent MBS for PC or EBA-GMA, a commonly used toughening agent for PBT, will seriously affect the flame retardant performance of the resin. There is a contradiction between toughness, especially low temperature toughness, and it is difficult to achieve it at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature-resistant PC alloy material and preparation method thereof
  • Low-temperature-resistant PC alloy material and preparation method thereof
  • Low-temperature-resistant PC alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] Unless otherwise defined, the technical terms used in the following embodiments have the same meaning as commonly understood by those skilled in the art to which the present invention belongs. The test reagents used in the following examples, unless otherwise specified, are conventional biochemical reagents; the experimental methods, unless otherwise specified, are conventional methods.

[0030] The present invention is described in detail below in conjunction with embodiment.

[0031] The PC resin uses PC S-2000F (Mitsubishi Japan) with a viscosity average molecular weight of 22,000; the PBT resin uses medium-viscosity PBT GX121 (Yizheng Petrochemical); the flame retardant uses RDT-7 (Weidong Chemical); other flame retardants use F -2100 (ICL) and FP-600 (Aidike); the first toughening agent is S-170H of Tailong Chemical (volume average particle size 350nm, rubber content 32%); the other first toughening agent is Mitsubishi Li Yang’s S-2001; the second toughening agent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a low-temperature-resistant PC alloy material and a preparation method thereof. The low-temperature-resistant PC alloy material comprises the following components in parts by weight: 70.0-90.0 parts of PC resin, 25.0-35.0 parts of a PBT resin, 5.0-15.0 part of a flame retardant, 2.0-10.0 parts of an auxiliary flame retardant, 2.0-15.0 parts of a first toughening agent, 1.0-5.0 parts of a second toughening agent, 0.01-2.0 parts of an antioxidant, and 0.01-1.2 parts of other auxiliary agents. The low-temperature-resistant PC alloy material provided by the invention has excellent low-temperature resistance, and is especially suitable for occasions with relatively high requirements on use environments, especially in the fields of household appliances, industrial machinesand the like which are in contact with oil stains and solvents and have requirements on low-temperature toughness.

Description

technical field [0001] The invention belongs to the field of engineering plastics, and in particular relates to a low-temperature-resistant PC alloy material and a preparation method thereof. Background technique [0002] Polycarbonate resin is a general-purpose engineering plastic, which has the advantages of transparency, impact resistance, heat resistance, dimensional stability, etc., but PC also has the problems of large internal stress, solvent resistance and difficult processing. PBT resin is a crystalline polymer with excellent solvent resistance and molding processability. Adding PBT to PC resin can significantly improve the processability and solvent resistance of PC; the improvement of solvent resistance is due to the formation of an interpenetrating network in which PBT, only when the crystallized PBT resin reaches a certain ratio, PC / PBT The solvent resistance of the alloy is greatly improved. [0003] When applied to home appliances, electrical appliances or i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L67/02C08L51/04C08L23/08
CPCC08L69/00C08L2205/035C08L2201/02C08L2203/20C08L67/02C08L51/04C08L23/0884
Inventor 董相茂陈勇文田征宇艾军伟岑茵佟伟
Owner TIANJIN KINGFA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com