Nano waterproof material for buildings and preparation method thereof

A waterproof material and technology for construction, applied in the direction of coating, etc., can solve the problems of poor waterproof performance, difficult construction, short service life, etc.

Inactive Publication Date: 2021-03-09
WEIFANG UNIV OF SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the early days, people used oil felt and asphalt as waterproof materials. However, using this material is not only very difficult to construct, but also has poor waterproof performance and short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano waterproof material for buildings and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The embodiment of the present invention also provides a method for preparing a nano-waterproof material for construction, which includes the following steps:

[0030] Preparation of mixed emulsion: mix acrylic resin and silicone acrylic emulsion, then add dodecyl alcohol ester dropwise while stirring, and obtain mixed emulsion after the stirring reaction is completed;

[0031] Mixing of filler additives: sieve diatomaceous earth, then put it into a blender with nano-titanium dioxide and nano-silica powder, first add 5-10 parts of water, then add dispersant, defoamer, bactericide and the remaining water, stir and mix to obtain filler additives;

[0032] Finished product preparation: Mix the mixed emulsion with filler additives, stir and react to get the finished product.

[0033]In the above examples, firstly, through the above mixed emulsion preparation steps, the acrylic resin and the silicone acrylic emulsion are mixed, and the dodecyl alcohol ester is added dropwise...

Embodiment 1

[0044] The embodiment of the present invention provides a nano-waterproof material for construction, which is prepared through the following steps:

[0045] Mixed emulsion preparation: Mix 50g of acrylic resin with 30g of silicone acrylic emulsion, then add 0.5g of dodecyl alcohol dropwise while stirring at 60-80°C, the stirring rate is 1000rpm, and react for 45min. After the stirring reaction is completed, a mixed emulsion is obtained;

[0046] Mixing of filler additives: Take 10g of diatomaceous earth and pass through a 300 mesh sieve, and then put 10g of nano-titanium dioxide with a particle size of 25nm and 1g of nano-silicon micropowder with a particle size of 60nm into a blender, first add 5g of water, and mix at 60 At ℃, add 0.5g of dispersant, 0.5g of defoamer, 0.2g of bactericide and the remaining 10g of water while stirring, stir at 1000rpm for 45min, and obtain the filler additive after stirring;

[0047] Finished product preparation: Mix the mixed emulsion and fill...

Embodiment 2

[0049] The embodiment of the present invention provides a nano-waterproof material for construction, which is prepared through the following steps:

[0050] Preparation of mixed emulsion: Mix 80g of acrylic resin with 40g of silicone acrylic emulsion, then add 2g of dodecyl alcohol dropwise while stirring at 60-80°C, the stirring rate is 2000rpm, and react for 90min. After the stirring reaction is completed, a mixed emulsion is obtained;

[0051] Mixing of filler additives: Take 20g of diatomite and pass through a 1000 mesh sieve, then put it into a blender with 20g of nano-titanium dioxide with a particle size of 5nm, and 10g of nano-silicon powder with a particle size of 30nm, first add 10g of water, and mix at 80 At ℃, add 1g of dispersant, 1g of defoamer, 1g of bactericide and the remaining 20g of water while stirring, stir at 2000rpm for 90min, and get the filler additive after mixing;

[0052] Preparation of finished product: Mix the mixed emulsion and filler additives, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a nano waterproof material for buildings and a preparation method thereof, and relates to the technical field of building materials. The invention discloses a nano waterproof material for buildings. The nano waterproof material is prepared from the following components: acrylic resin, silicone acrylic emulsion, Texanol, diatomite, nano titanium dioxide, nano silica powder, adispersing agent, an antifoaming agent, a bactericide and water. The material is excellent in waterproof performance and long in service life. In addition, the invention further provides a preparation method of the nano waterproof material for the building. The preparation method comprises the following steps: preparing a mixed emulsion, mixing the filler and the auxiliary agent, and preparing afinished product. The method is simple in process, and the prepared product is good in waterproof performance and long in service life.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a nano waterproof material for building and a preparation method thereof. Background technique [0002] The waterproof problem of buildings is not only related to people's work and living environment, but also affects the service life of buildings. With the rapid development of the national economy, my country's engineering construction is also booming, especially the construction of various projects such as housing, sports facilities, and road traffic, which provide material conditions for improving people's living standards. How to do a good job in various engineering constructions Waterproof and corrosion resistance issues are the most concerned issues of the project construction party. To overcome technical difficulties, we must rely on scientific and technological progress and adopt advanced technologies, including the application of new materials. [0003] In the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/00C09D133/04C09D7/61C09D7/63
CPCC08K2003/2241C08K2201/011C09D133/00C09D7/61C09D7/63C09D7/67C09D7/70C08L43/04C08K13/04C08K7/26C08K3/22C08K3/36C08K5/10
Inventor 张钦刚肖飞周超张玉明
Owner WEIFANG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap