Converter smelting process of HRB400cE corrosion-resistant steel

A converter smelting and corrosion-resistant steel technology, which is applied in the iron and steel manufacturing process, process efficiency improvement, metal processing, etc., can solve the problem of low smelting efficiency

Active Publication Date: 2021-03-19
福建三宝钢铁有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Therefore, the present invention provides a converter smelting process for HRB400cE corrosion-resistant steel to overcome the problem of low smelting efficiency caused by the inability to effectively decarburize molten steel with different carbon contents in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Converter smelting process of HRB400cE corrosion-resistant steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0066] In order to make the objects and advantages of the present invention clearer, the present invention will be further described below in conjunction with the examples; it should be understood that the specific examples described here are only for explaining the present invention, and are not intended to limit the present invention.

[0067] Preferred embodiments of the present invention are described below with reference to the accompanying drawings. Those skilled in the art should understand that these embodiments are only used to explain the technical principle of the present invention, and are not intended to limit the protection scope of the present invention.

[0068] It should be noted that, in the description of the present invention, terms such as "upper", "lower", "left", "right", "inner", "outer" and other indicated directions or positional relationships are based on the terms shown in the accompanying drawings. The direction or positional relationship shown is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a converter smelting process for HRB400cE corrosion-resistant steel. The converter smelting process comprises the following steps that a converter is checked; smelting raw materials are fed into the converter, and heating is carried out to liquefy the smelting raw materials in the converter into molten steel; an oxygen lance is inserted into the converter and introduces oxygen above the molten steel to decarburize the molten steel; the molten steel decarburization progress is judged according to the flame brightness and whether decarburization is completed or not is judged according to the oxygen lance outline definition; a carburant is added into the converter to primarily remove oxygen in the molten steel; the molten steel is conveyed to a steel ladle, and silicon-manganese alloy is added to conduct secondary deoxygenation on the molten steel; and corresponding types of metal are selected to perform alloying treatment on the molten steel. A preset matrix is established by using a central control processor, the oxygen introduction duration of the oxygen lance is determined according to the carbon content in the molten steel, so that the oxygen introduced by the oxygen lance just reacts with the carbon element in the molten steel, so that the molten steel is decarburized by using the specified amount of oxygen, the decarburization efficiency of the process for the molten steel is effectively improved, and therefore, the smelting efficiency of the process is improved.

Description

technical field [0001] The invention relates to the technical field of metal smelting, in particular to a converter smelting process for HRB400cE corrosion-resistant steel. Background technique [0002] HRB400cE is the grade of threaded steel bar stipulated in "Steel for Reinforced Concrete" GB 1499.2-2007. Due to the wide range of standard components and the differences in production equipment and process control of manufacturers, the composition of HRB400cE hot-rolled ribbed steel bars produced by various manufacturers Each is different, and the production process of each steel factory is also different. In the prior art, the corrosion resistance of HRB400cE steel is usually improved by removing the carbon in the raw material or adding metals during the smelting process to alloy the molten steel. , at the same time, in the prior art, there is no way to accurately adjust the amount of oxygen in the process of passing oxygen to molten steel according to the carbon content i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C5/28C21C5/30
CPCC21C5/28C21C5/30C21C2300/06Y02P10/20Y02P10/25
Inventor 王光文陈贵和张盛梁涂文兴
Owner 福建三宝钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com