High-melt-strength polypropylene material as well as preparation method and application thereof

Abstract

The invention discloses a high-melt-strength polypropylene material as well as a preparation method and application thereof. The high-melt-strength polypropylene material comprises the components in parts by weight: 10-90 parts of straight-chain polypropylene, 0.5-50 parts of polypropylene with a long branched chain, and 0.01-20 parts of a fluorine compound. Long molecular chains of straight-chain polypropylene are utilized to increase entanglement among the molecular chains, thereby being beneficial to enhancing the stability of the melt during extrusion and plastic uptake; by adding the polypropylene with the long branched chain and utilizing the branched chain structure, the melt strength can be greatly improved; and the fluorine compound is not molten in the forming process, and can be stretched into fibers under the action of the melt, so that the polypropylene molecular chain and the fluorine compound fibers form an interpenetrating network, and the melt strength of the whole material is further improved. The polypropylene material prepared in the method has high melt strength, and is mainly suitable for blow molding, plastic uptake and other occasions.

Description

technical field [0001] The invention relates to the technical field of engineering plastics, in particular to a high-melt-strength polypropylene material and its preparation method and application. Background technique [0002] Polypropylene material is currently the most used polymer material. It has excellent processing properties and mechanical properties. It is widely used in daily life and industrial production fields, such as: agricultural film, wire and cable, communication, housing construction and aviation manufacturing. Wait. [0003] At present, the polyolefin materials suitable for blow molding and blister use are basically pure HDPE or PP resins. These resins can be molded well, but they still need to be improved in terms of heat resistance and strength. In the industry, the high strength and high rigidity of glass fibers are usually used to improve product strength and heat resistance, but conventional glass fiber reinforced polypropylene materials have low me...

AI Technical Summary

Problems solved by technology

[0003] At present, the polyolefin materials suitable for blow molding and blister use are basically pure HDPE or PP resins. These resins can be molded well, but they still need to be improved in terms of heat resistance and strength.

In the industry, the high strength and high rigidity of glass fibers are usually used to improve product strength and heat resistance, but conventional glass fiber reinforced polypropylene materials have low melt strength, low melt elongation, surface floating fibers and poor toughness And other issues