A kind of mxene-v2c modified carbon fiber fabric self-lubricating material and preparation method thereof

A carbon fiber fabric, self-lubricating material technology, applied in the field of friction materials

Active Publication Date: 2021-11-12
LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Mxene-V not seen 2 Related reports on the application of C in tribology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mxene-v2c modified carbon fiber fabric self-lubricating material and preparation method thereof
  • A kind of mxene-v2c modified carbon fiber fabric self-lubricating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The present invention provides the above-mentioned Mxene-V 2 The preparation method of the carbon fiber fabric self-lubricating material of C modification, comprises the following steps:

[0023] (1) Mxene-V 2 C, phenolic resin and polar organic solvent are mixed, carry out ultrasonication, obtain coating liquid;

[0024] (2) The carbon fiber fabric is immersed in the coating solution, and the obtained impregnated carbon fiber fabric is dried to obtain Mxene-V 2 C modified carbon fiber fabric self-lubricating material.

[0025] The present invention will Mxene-V 2 C. Mix the phenolic resin and the polar organic solvent, and perform ultrasonic to obtain the coating liquid. The present invention has no special requirements on the phenolic resin, and the phenolic resin well known to those skilled in the art can be used. As a specific embodiment of the present invention, the phenolic resin is Tiemao brand 204 phenolic resin produced by Shanghai Xinguang Chemical Co., L...

Embodiment 1

[0037] (1) Phenolic resin, ethanol and Mxene-V with a sheet diameter of 20 μm 2 C is dispersed according to the mass of 30g: 60g: 0.4g for 32min under 500W ultrasonic conditions to obtain the coating solution;

[0038] (2) The specification is 1K, the density in the warp direction is 10 pieces / 10mm, the density in the weft direction is 10 pieces / 10mm, and the mass per unit area is 125g / m 2 The carbon fiber fabric was immersed in the above coating solution for 15 minutes, and then moved to a blast oven at 75°C to dry for 45 minutes. The dipping process was repeated until the weight of the blended fiber cloth increased by 50%, and Mxene-V was obtained. 2 C is a carbon fiber fabric self-lubricating material with a load of 2.5% of the fiber cloth mass;

[0039] (3) Paste the above self-lubricating material on the surface of the titanium alloy with phenolic resin, apply a pressure of 0.2 MPa, raise it from room temperature to 150 °C at a rate of 7 °C / min, and form it after curing ...

Embodiment 2

[0042] (1) An organic solvent mixed with phenolic resin, ethanol and acetone, and Mxene-V with a sheet diameter of 25 μm 2 C is dispersed by mass 20g:40g:0.1g for 35min under 550W ultrasonic conditions to obtain a coating solution;

[0043] (2) The specification is 1K, the warp density is 10 / 10mm, the weft density is 10 / 10mm, and the mass per unit area is 120g / m 2 The carbon fiber fabric was immersed in the above coating solution for 10 minutes, and then moved to a 70°C blast oven to dry for 30 minutes. The dipping process was repeated until the weight of the blended fiber cloth increased by 40%, and Mxene-V was obtained. 2 C load is 0.8% of the carbon fiber fabric self-lubricating material of the fiber cloth mass;

[0044] (3) Paste the above-mentioned self-lubricating material on the surface of 304 steel with phenolic resin, apply a pressure of 0.1MPa, raise it from room temperature to 120°C at a rate of 5°C / min, and form it after curing for 2 hours, which is recorded as 2#...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a Mxene‑V 2 A C-modified carbon fiber fabric self-lubricating material and a preparation method thereof belong to the technical field of friction materials. Mxene‑V 2 Under the action of frictional shear stress, its sheets are very easy to slip, which can reduce the interfacial shear strength, thereby reducing the coefficient of friction; at the same time, Mxene‑V 2 The C surface has a large amount of F ‑ , OH ‑ Functional groups can improve the interfacial bonding characteristics with carbon fiber fabrics, and good interfacial bonding strength can improve the stress transfer and wear life of self-lubricating materials. The present invention will Mxene-V 2 C is introduced into the carbon fiber fabric, and the resulting carbon fiber fabric self-lubricating material has a low coefficient of friction. The results of the embodiment show that the Mxene-V provided by the invention 2 The carbon fiber fabric self-lubricating material modified by C is between 0.101 and 0.125, and has good tribological properties.

Description

technical field [0001] The invention relates to the technical field of friction materials, in particular to a Mxene-V 2 C modified carbon fiber fabric self-lubricating material and preparation method thereof. Background technique [0002] Carbon fiber fabric reinforced composites have been widely used in aircraft, automobiles, railway equipment, aerospace equipment and defense industries due to their outstanding advantages such as self-lubrication, low cost, easy processing, chemical stability and light weight. At present, fillers such as graphite, molybdenum disulfide, and polytetrafluoroethylene are mostly used in the existing technology to improve the self-lubricating ability of carbon fiber fabrics. However, poor wear resistance is still a bottleneck that restricts its long-term use under complex and harsh working conditions. . Mxene is a new type of transition metal carbide or nitride two-dimensional crystal, which is prepared by selectively etching the A atomic layer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/06C08K3/14C08K7/06
CPCC08K3/14C08K7/06C08L61/06
Inventor 赵普王齐华李宋徐明坤陶立明张耀明张新瑞王廷梅
Owner LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com