Preparation process of aluminum foil composite material

A composite material and preparation technology, applied in the field of flexible packaging, can solve the problems of poor barrier performance of aluminum foil composite materials, single function of aluminum foil composite materials, and failure to satisfy users, etc., to achieve excellent barrier performance, good use effect and low manufacturing cost cheap effect

Inactive Publication Date: 2021-05-28
嘉兴奥飞新材料科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The development prospects of aluminum foil packaging are very broad; composite aluminum foil packaging has the advantages of high barrier performance, light weight, anti-ultraviolet, and long shelf life at room temperature. With the progress, people's requirements for aluminum foil composite materials are getting higher and higher, resulting in the existing preparation methods of aluminum foil composite materials can no longer meet the needs of users;
[0003] There are certain disadvantages when the existing aluminum foil composite material preparation method is used. First, the entire production process of the existing aluminum foil composite material preparation method is relatively complicated, and the aluminum foil composite material produced has a single function and the use effect is not good. Secondly, the produced aluminum foil During the winding process of the composite material, due to the continuous increase of the volume between the film rolls, there will be uneven force during winding, and a lot of air will be involved, which will cause the aluminum foil composite material to wrinkle and make the barrier of the aluminum foil composite material The performance deteriorates and does not meet people's requirements for use. Therefore, we propose a preparation process for aluminum foil composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of aluminum foil composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of an aluminum foil composite material preparation process, the preparation method comprises specific steps as follows:

[0027] (1), activated carbon carbon powder, silver powder and water-absorbing powder are sent into the mixing center and stirred to obtain mixed powder;

[0028] Before stirring, activated carbon carbon powder, silver powder and water-absorbing powder are screened, and 70-80 mesh screens are used during screening. The weight ratio of activated carbon carbon powder, silver powder and water-absorbing powder is 3.2:2.1:1.2 during screening;

[0029] The stirring speed of activated carbon carbon powder, silver powder and water-absorbing powder is 32r / min, and the stirring time is 25 seconds.

[0030] (2), add the mixed powder into the polyvinyl alcohol solution, and stir in a water bath to obtain a mixed solution:

[0031] The ratio of the mixed powder to the polyvinyl alcohol solution is 1:4, the temperature of the water bath is 55...

Embodiment 2

[0040] A preparation method of an aluminum foil composite material preparation process, the preparation method comprises specific steps as follows:

[0041] (1), activated carbon carbon powder, silver powder and water-absorbing powder are sent into the mixing center and stirred to obtain mixed powder;

[0042] Before stirring, activated carbon carbon powder, silver powder and water-absorbing powder are screened, and 70-80 mesh screens are used during screening, and the weight ratio of activated carbon carbon powder, silver powder and water-absorbing powder is 3.9:2.7:1.6 during screening;

[0043] The stirring speed of activated carbon carbon powder, silver powder and water-absorbing powder is 32r / min, and the stirring time is 25 seconds.

[0044] (2), add the mixed powder into the polyvinyl alcohol solution, and stir in a water bath to obtain a mixed solution:

[0045] The ratio of the mixed powder to the polyvinyl alcohol solution is 1:4, the temperature of the water bath i...

Embodiment 3

[0054] A preparation method of an aluminum foil composite material preparation process, the preparation method comprises specific steps as follows:

[0055] (1), activated carbon carbon powder, silver powder and water-absorbing powder are sent into the mixing center and stirred to obtain mixed powder;

[0056] Activated carbon carbon powder, silver powder and water-absorbing powder are screened before stirring, and 70-80 mesh screens are used during screening, and the weight ratio of activated carbon carbon powder, silver powder and water-absorbing powder is 4.5:3.3:1.9 during screening;

[0057] The stirring speed of activated carbon carbon powder, silver powder and water-absorbing powder is 32r / min, and the stirring time is 25 seconds

[0058] (2) Add the mixed powder to the polyvinyl alcohol solution and stir in a water bath to obtain a mixed solution:

[0059]The ratio of the mixed powder to the polyvinyl alcohol solution is 1:4, the temperature of the water bath is 55 de...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process of an aluminum foil composite material. The process comprises the following specific steps: feeding and intensively stirring activated carbon powder, silver powder and water absorption powder to obtain mixed powder; and adding the mixed powder into a polyvinyl alcohol solution, and stirring in a water bath. According to the preparation process of the aluminum foil composite material, a mixed layer capable of adsorbing different colors and peculiar smells and having a sterilization effect can be formed on the surface of aluminum foil, food can be better packaged, the use effect is better, the aluminum foil is not prone to being broken and pinholes are not prone to being formed when the prepared aluminum foil composite material is folded, in addition, the strength of the aluminum foil composite material is improved, so that the aluminum foil composite material is not prone to damage, a diameter of a pressing roller is always smaller than that of a film roll during rolling, a wrap angle formed by the prepared aluminum foil composite material film and the pressing roller is reduced, rolled air is less, the film roll is neat, the excellent barrier property can be kept, and the use effect is better.

Description

technical field [0001] The invention relates to the technical field of flexible packaging, in particular to a preparation process of an aluminum foil composite material. Background technique [0002] Because of its excellent characteristics, aluminum foil is widely used in food, beverages, cigarettes, medicines, household daily necessities, etc., and is usually used as its packaging material. The development prospects of aluminum foil packaging are very broad; composite aluminum foil packaging has the advantages of high barrier performance, light weight, anti-ultraviolet, and long shelf life at room temperature. With the progress, people's requirements for aluminum foil composite materials are getting higher and higher, resulting in the existing preparation methods of aluminum foil composite materials can no longer meet the needs of users; [0003] There are certain disadvantages when the existing aluminum foil composite material preparation method is used. First, the entir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B65D65/40B65H18/26B32B15/09B32B15/20B32B27/36B32B38/16
CPCB65D65/40B65H18/26B32B15/09B32B15/20B32B27/36B32B38/164B32B2038/166
Inventor 宋奇加谈飞顺
Owner 嘉兴奥飞新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products