Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Hyaluronic acid cow leather mat preparation process

A preparation process, a technology of hyaluronic acid, applied in the directions of leather drying, leather surface treatment, leather surface mechanical treatment, etc., to achieve the effect of deepening and brightening mercerizing effect, excellent solvent resistance, and good cross-linking effect.

Active Publication Date: 2021-07-23
CHONGQING LONGFA LEATHER PROD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention intends to provide a preparation process of hyaluronic acid cowhide mat to solve the problem of combining hyaluronic acid and cowhide mat in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hyaluronic acid cow leather mat preparation process
  • Hyaluronic acid cow leather mat preparation process
  • Hyaluronic acid cow leather mat preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A hyaluronic acid cowhide mat preparation process is characterized in that: comprising the following steps,

[0042] Step (1), preparing raw materials: including the following raw materials in parts by mass, 8 parts of hand feeling agent, 6 parts of penetrating agent, 25 parts of fixative and 8 parts of hyaluronic acid;

[0043] In this embodiment, the hand feeling agent is water-based silicone emulsifiable oil, and the fixing agent is polyurethane resin.

[0044] Step (2), mixing raw materials: stirring and mixing the hand feeling agent, penetrating agent and fixing agent to make a mixed tanning agent, and the stirring time is 20-30 minutes;

[0045]Step (3), standing still: the mixed tanning agent prepared in step (2) is left standing for 12h to 48h;

[0046] Step (4), stirring: adding hyaluronic acid to the mixed tanning agent after standing still and stirring to obtain a mixed solution; the stirring time is 10-20 minutes;

[0047] Step (5), spraying: spray the mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of cow leather mat preparation, and discloses a hyaluronic acid cow leather mat preparation process which comprises the following steps of (1), preparing raw materials including the following raw materials in parts by mass: 8-15 parts of a hand feeling agent, 6-15 parts of a penetrating agent, 25-40 parts of a fixing agent and 8-12 parts of hyaluronic acid, (2) raw material mixing: stirring and mixing the hand feeling agent, the penetrating agent and the fixing agent to prepare a mixed tanning agent, (3) standing: standing the mixed tanning agent prepared in the step (2) for 12-48 hours, (4) stirring: adding hyaluronic acid into the mixed tanning agent after standing, and stirring to obtain a mixed solution, (5) spraying: spraying the mixed solution stirred in the step (4) on the surface of the cow leather mat for at least two times, and (6) shaping, specifically, enabling the cow leather mat sprayed in the step (5) to be subjected to hot pressing shaping. The problem that hyaluronic acid and the cow leather mat are mutually combined for application in the prior art is effectively solved.

Description

technical field [0001] The invention relates to the technical field of preparation of cowhide mats, in particular to a preparation process of hyaluronic acid cowhide mats. Background technique [0002] Natural cowhide has strong antibacterial properties, and the cowhide mat has been treated with scientific technology to prevent mold and moths. At the same time, the cowhide mat has a smooth surface, is not easy to hide dirt, and will not cause mites to breed. Therefore, it is popular among the general public. Welcome. [0003] With the continuous improvement of living standards, consumers have a higher pursuit of leather mats. In the beauty industry, "hyaluronic acid" moisturizing is a well-known common sense. How to apply hyaluronic acid to leather mats is still lacking. The research on the combination of mats, although the invention patent with the publication number CN110680141A in the prior art discloses a composite braided summer mat based on hyaluronic acid, which is m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C14C11/00C14B1/58C14B1/44A47G9/02
CPCC14C11/00C14B1/58C14B1/44A47G9/0238A47G2400/10
Inventor 何海东
Owner CHONGQING LONGFA LEATHER PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com