A kind of aluminum alloy casting heat treatment device

A heat treatment device and technology for aluminum alloy castings, applied in the field of aluminum alloy casting, can solve the problems of easy deformation of castings, uneven cooling, and the movement of aluminum alloy castings is not smooth enough to achieve the effect of improving efficiency and avoiding deformation.

Active Publication Date: 2022-07-12
临沂大田标准件有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Currently, spraying with water is a common method for cooling aluminum alloy castings; however, this method easily leads to uneven cooling, easy deformation of castings, and the movement of aluminum alloy castings in the cooling mechanism is not smooth enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of aluminum alloy casting heat treatment device
  • A kind of aluminum alloy casting heat treatment device
  • A kind of aluminum alloy casting heat treatment device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The present invention will be further described below in conjunction with the accompanying drawings.

[0030] see e.g. Figure 1 to Figure 7 As shown, the technical solution adopted in this specific embodiment is: it includes a water cooling mechanism 1 and an air cooling mechanism 2; the water cooling mechanism 1 includes a box body 1-1, an observation window 1-2, a scale marking layer 1-3, Thermometer 1-4, No. 1 conveyor belt 1-5, No. 1 limit plate 1-6, No. 1 transmission motor 1-7, No. 1 mounting plate 1-8, No. 2 conveyor belt 1-10, No. 2 transmission motor 1- 11. No. 1 connecting rod 1-12, No. 1 guide plate 1-13, No. 2 mounting plate 1-14, No. 1 water pump 1-15, No. 1 water pipe 1-16, No. 2 water pipe 1-17, No. 3 water pipe 1- 18. No. 4 water pipe 1-19, atomizing nozzle 1-20 and guide roller 1-21; box 1-1 is an upper-side open structure; the right opening of the front side wall of box 1-1 is embedded There is an observation window 1-2, which is helpful to observe ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A heat treatment device for aluminum alloy castings, the invention relates to the technical field of aluminum alloy casting. They are respectively placed on the front and rear inner side walls of the box body; several No. 1 limit plates are fixed at equal distances on the outer belt surface of the No. 1 conveyor belt, and the No. 1 limit plates are set obliquely. They are respectively placed on the front and rear inner walls of the box; it is convenient to move the aluminum alloy castings, which improves the moving efficiency; the aluminum alloy castings can be cooled evenly to avoid deformation; the water droplets on the aluminum alloy castings can be blown off in time, so that the aluminum alloy castings can be blown off in time. The castings are drained for the next processing.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy casting, in particular to a heat treatment device for aluminum alloy castings. Background technique [0002] Heat treatment is an indispensable part of improving the performance of metal materials. Many metal heat treatment materials require rapid cooling, such as quenching of metal materials and solution treatment of austenitic stainless steel. The faster the cooling rate, the better the properties of the material can be achieved. [0003] At present, water spraying is a common method for cooling aluminum alloy castings; however, this method easily leads to uneven cooling, easy deformation of castings, and the movement of aluminum alloy castings in the cooling mechanism is not smooth enough. SUMMARY OF THE INVENTION [0004] The purpose of the present invention is to propose a heat treatment device for aluminum alloy castings in view of the defects and deficiencies of the prior art, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/04
CPCC22F1/04C22F1/002Y02P10/20
Inventor 李珊珊
Owner 临沂大田标准件有限公司