Medical adhesive material for vascular closure and preparation method thereof
A technology of vascular closure and modification, which is applied in the field of medical adhesive materials for vascular closure, can solve the problems of poor hemostasis performance and achieve the effects of increasing film-forming performance, good biocompatibility and good adsorption performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] The preparation method of the medical adhesive material for vascular closure described in this embodiment comprises the following steps:
[0025] (1) take a certain amount of chitosan and be dissolved in 1% HAc solution and mix well, and constantly add the acetone solution containing succinic anhydride in the stirring process, control the consumption of succinic anhydride to account for the quality of chitosan 30wt% of 30 wt%, at 40°C for heat preservation modification reaction for 8 hours; after the reaction is completed, filter and collect the solid phase and add ethanol to soak for a period of time, filter and collect the precipitate, dissolve it in distilled water, add 3 times the volume of acetone to precipitate, and collect the precipitate Then wash with ethanol and acetone successively, and dry to obtain the required N-succinylated chitosan, which is set aside;
[0026] (2) According to the mass ratio of 1:0.8:2, the above-mentioned N-succinylated chitosan, gluco...
Embodiment 2
[0029] The preparation method of the medical adhesive material for vascular closure described in this embodiment comprises the following steps:
[0030] (1) take a certain amount of chitosan and be dissolved in 1% HAc solution and mix well, and constantly add the acetone solution containing succinic anhydride in the stirring process, control the consumption of succinic anhydride to account for the quality of chitosan 30wt% of 30 wt%, at 40°C for heat preservation modification reaction for 8 hours; after the reaction is completed, filter and collect the solid phase and add ethanol to soak for a period of time, filter and collect the precipitate, dissolve it in distilled water, add 3 times the volume of acetone to precipitate, and collect the precipitate Then wash with ethanol and acetone successively, and dry to obtain the required N-succinylated chitosan, which is set aside;
[0031] (2) According to the mass ratio of 1:0.5:1, the above-mentioned N-succinylated chitosan, gluco...
Embodiment 3
[0034] The preparation method of the medical adhesive material for vascular closure described in this embodiment comprises the following steps:
[0035] (1) take a certain amount of chitosan and be dissolved in 1% HAc solution and mix evenly, and constantly add the acetone solution containing succinic anhydride in the stirring process, control the consumption of succinic anhydride to account for the mass of chitosan 30wt% of 30 wt%, at 40°C for heat preservation modification reaction for 8 hours; after the reaction is completed, filter and collect the solid phase and add ethanol to soak for a period of time, filter and collect the precipitate, dissolve it in distilled water, add 3 times the volume of acetone to precipitate, and collect the precipitate Then wash with ethanol and acetone successively, and dry to obtain the required N-succinylated chitosan, which is set aside;
[0036] (2) According to the mass ratio of 1:1:3, the above-mentioned N-succinylated chitosan, glucoman...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap