Epoxy resin crack pouring adhesive for repairing cement concrete cracks and preparation method of epoxy resin crack pouring adhesive
A technology of cement concrete and water-based epoxy resin, applied in the direction of epoxy resin glue, adhesive, monocarboxylic acid ester copolymer adhesive, etc., can solve the problems of low elongation, cracking, low bonding strength, etc. adhesive effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0043] Example 1
[0044] An epoxy resin joint glue for repairing cement concrete cracks
[0045] Its composition and content are in parts by mass:
[0046] Component A: 20 parts of water-based epoxy resin emulsion, 5 parts of water-based polyurethane, 5 parts of acrylate emulsion, 30 parts in total;
[0047] Component B: 20 parts of water-based epoxy curing agent, 2 parts of talcum powder, 0.2 parts of silane coupling agent, 0.2 parts of ultraviolet absorber, 24 parts of ultrafine cement, 12.3 parts of self-repairing microspheres, 1.2 parts of cement expansion agent, defoaming 0.1 part of dose, a total of 60 parts;
[0048] Component C: 5 parts of water;
[0049] Wherein the self-healing microspheres are prepared according to the following steps:
[0050] The first step: preparation of self-healing microsphere core material:
[0051] Weigh 6 parts of superabsorbent resin, 3.9 parts of superfine cement, and 0.1 part of silane coupling agent, mix and stir evenly, and obt...
Example Embodiment
[0071] Example 2
[0072] An epoxy resin joint glue for repairing cement concrete cracks
[0073] Its composition and content are in parts by mass:
[0074] Component A: 21.5 parts of water-based epoxy resin emulsion, 4.5 parts of water-based polyurethane, 4 parts of acrylate emulsion, 30 parts in total;
[0075] Component B: 21.5 parts of water-based epoxy curing agent, 1.8 parts of talcum powder, 0.2 parts of silane coupling agent, 0.2 parts of ultraviolet absorber, 23.5 parts of ultrafine cement, 11.5 parts of self-repairing microspheres, 1.2 parts of cement expansion agent, 0.1 part of foaming agent, 60 parts in total;
[0076] Component C: 7 parts of water;
[0077] Wherein the self-healing microspheres are prepared according to the following steps:
[0078] The first step: preparation of self-healing microsphere core material:
[0079] Weigh 5.5 parts of superabsorbent resin, 4.4 parts of superfine cement, and 0.1 part of silane coupling agent, mix and stir evenly, ...
Example Embodiment
[0099] Example 3
[0100] An epoxy resin joint glue for repairing cement concrete cracks
[0101] Its composition and content are in parts by mass:
[0102] Component A: 22.5 parts of water-based epoxy resin emulsion, 4 parts of water-based polyurethane, 3.5 parts of acrylate emulsion, 30 parts in total;
[0103] Component B: 22.5 parts of water-based epoxy curing agent, 1.5 parts of talc powder, 0.1 part of silane coupling agent, 0.1 part of ultraviolet absorber, 23 parts of ultrafine cement, 11.6 parts of self-repairing microspheres, 1.1 parts of cement expansion agent, 0.1 part of foaming agent, 60 parts in total;
[0104]Component C: 8 parts of water;
[0105] Wherein the self-healing microspheres are prepared according to the following steps:
[0106] The first step: preparation of self-healing microsphere core material:
[0107] Weigh 5 parts of superabsorbent resin, 4.9 parts of superfine cement, and 0.1 part of silane coupling agent, mix and stir evenly, and obtai...
PUM
Property | Measurement | Unit |
---|---|---|
Amine value | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap