Long-service-life colored pervious concrete and preparation method thereof

A technology of permeable concrete and preparation method, which is applied in the field of concrete to achieve the effects of prolonging service life and improving compressive properties

Inactive Publication Date: 2022-01-04
祝福来
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of color permeable concrete with high service life and its preparation method in view of the existing problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A preparation method of color permeable concrete with high service life, comprising the following steps:

[0045] (1) Weighing of raw materials:

[0046] Weigh 1200 parts of stones, 360 parts of cement, 10 parts of reinforcing agent, 100 parts of water, 6 parts of colorant and 2 parts of protective agent in corresponding parts by weight. 2 parts of thickener, 1 part of rubber powder, 5 parts of accelerator, 5 parts of water reducer, 2 parts of air-entraining agent;

[0047] (2) High pressure homogeneous treatment:

[0048] Place the reinforcing agent and coloring agent weighed in step (1) in sequence in a high-pressure homogenizer for high-pressure homogenization, control the working pressure to 90 MPa, and take out the mixture A after high-pressure homogenization for 1 hour for later use;

[0049] (3) variable speed stirring treatment:

[0050] First add the stones and cement weighed in the step (1) into the mixing tank at a low speed of 400rpm and mix well, then ad...

Embodiment 2

[0058] A preparation method of color permeable concrete with high service life, comprising the following steps:

[0059] (1) Weighing of raw materials:

[0060] Weigh 1600 parts of stones, 405 parts of cement, 17.5 parts of reinforcing agent, 125 parts of water, 13.5 parts of colorant, and 3 parts of protective agent in corresponding parts by weight. 2.5 parts of thickener, 1.5 parts of rubber powder, 12.5 parts of accelerator, 12.5 parts of water reducer, 4 parts of air-entraining agent;

[0061] (2) High pressure homogeneous treatment:

[0062]Place the reinforcing agent and coloring agent weighed in step (1) in sequence in a high-pressure homogenizer for high-pressure homogenization, control the working pressure to 100 MPa, and take out the mixture A after high-pressure homogenization for 1.5 hours for later use;

[0063] (3) variable speed stirring treatment:

[0064] First add the stones and cement weighed in the step (1) into the mixing tank at a low speed of 500rpm a...

Embodiment 3

[0072] A preparation method of color permeable concrete with high service life, comprising the following steps:

[0073] (1) Weighing of raw materials:

[0074] Weigh 2000 parts of stones, 450 parts of cement, 25 parts of reinforcing agent, 150 parts of water, 20 parts of colorant, and 4 parts of protective agent in corresponding parts by weight. 3 parts of thickener, 2 parts of rubber powder, 20 parts of accelerator, 20 parts of water reducing agent, 6 parts of air-entraining agent;

[0075] (2) High pressure homogeneous treatment:

[0076] Place the reinforcing agent and coloring agent weighed in step (1) in sequence in a high-pressure homogenizer for high-pressure homogenization, control the working pressure to 110MPa, and take out the mixture A after high-pressure homogenization for 2 hours for later use;

[0077] (3) variable speed stirring treatment:

[0078] First add the stones and cement weighed in the step (1) into the mixing tank at a low speed of 600rpm and mix ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of long-service-life colored pervious concrete, and belongs to the technical field of concrete. The method comprises the following steps: (1) weighing raw materials; (2) performing high-pressure homogenization treatment; (3) performing variable-speed stirring treatment; (4) performing cryogenic-ultrasonic coupling treatment; and (5) performing stirring treatment. According to the preparation method of the long-service-life colored pervious concrete, the technologies of high-pressure homogenization, variable-speed stirring, cryogenic-ultrasonic coupling treatment and the like are applied to processing and manufacturing of the concrete, so that the compression resistance and the water permeability of the concrete are remarkably improved, and experimental results show that the compressive strength and the permeability coefficient of the concrete prepared by the method are obviously superior to those of a control group, and the service life of the pervious concrete is more effectively prolonged.

Description

technical field [0001] The invention belongs to the technical field of concrete, and in particular relates to a color permeable concrete with high service life and a preparation method thereof. Background technique [0002] Permeable concrete is an important part of sponge city construction. At present, my country's urbanization level is developing rapidly, and in the process of urbanization, non-permeable cement concrete pavement has gradually replaced the original green vegetation, changing the natural soil vegetation and the natural permeable properties of the underlying layer. This change has brought about a series of ecological problems. In rainy weather, due to the existence of impermeable cement concrete, rainwater will accumulate on the surface to form surface runoff, and the water from surface runoff generally enters rivers through the urban drainage system. In lakes and seas, groundwater cannot be replenished. Since the "sponge city" policy was put forward, the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
CPCC04B28/00C04B2111/00284C04B2111/0075C04B2201/50C04B14/02C04B2103/0068C04B2103/54C04B2103/302C04B2103/12C04B2103/44C04B2103/304C04B18/12C04B24/24
Inventor 祝福来
Owner 祝福来
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap