A heat treatment method and a technology for drill steel, which are applied in the field of production and manufacture of drill steel, and can solve problems such as unseen heat treatment process methods.

Pending Publication Date: 2022-01-28
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are many patent documents and articles on steel for rock drilling tools and its manufacturing method in China. For example, the patent document whose publication number is CN 108504938 A discloses a production method of hollow steel for rock drilling tool

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1:

[0020] (1) forging the blank, the blank will be placed in the heating furnace at a temperature of 500 ℃ -600 ℃ holding section, holding time ≥2H, then heated to 1200 ± 10 ℃ at / h heating rate of 100 deg.] C, incubated ≥4h ; baked fast forging, open forging temperature ≥1050 ℃, compression molding;

[0021] (2) pre-heat treatment, compression molding of normalizing the initial product, incubated 4h 840 ℃, furnace cooling to 300 ℃, cooled baked, and then tempering, the heating temperature of 480 deg.] C 8h baked heat insulation air-cooling, for the next step step of laying the foundation;

[0022] (3) roughing, finishing, the lathe roughing, the surface of the oxide layer off the car, and precise control of the size, shape finishing producing finished; drilling using drilling drill holes, removing burrs around the hole, allowing drill rod and solder products supporting the use of normal;

[0023] (4) heat treatment process, is heated to a temperature of 940 ± 10...

Example Embodiment

[0026] Example 2:

[0027] (1) forging the blank, the blank will be placed in the heating furnace at a temperature of 600 ℃ -700 ℃ holding section, holding time ≥2H, then heated to 1200 ± 10 ℃ at / h heating rate of 100 deg.] C, incubated ≥4h ; baked fast forging, open forging temperature ≥1050 ℃, compression molding;

[0028] (2) pre-heat treatment, compression molding of normalizing the initial product, incubated 4h 840 ℃, furnace cooling to 300 ℃, cooled baked, and then tempering, the heating temperature of 480 deg.] C 8h baked heat insulation air-cooling, for the next step step of laying the foundation;

[0029] (3) roughing, finishing, the lathe roughing, the surface of the oxide layer off the car, and precise control of the size, shape finishing producing finished; drilling using drilling drill holes, removing burrs around the hole, allowing drill rod and solder products supporting the use of normal;

[0030] (4) heat treatment process, is heated to a temperature of 950 ± 10...

Example Embodiment

[0033] Example 3:

[0034] (1) forging the blank, the blank will be placed in the heating furnace at a temperature of 700 ℃ -800 ℃ holding section, holding time ≥2H, then heated to 1200 ± 10 ℃ at / h heating rate of 100 deg.] C, incubated ≥4h ; baked fast forging, open forging temperature ≥1050 ℃, compression molding;

[0035] (2) pre-heat treatment, compression molding of normalizing the initial product, incubated 4h 840 ℃, furnace cooling to 300 ℃, cooled baked, and then tempering, the heating temperature of 480 deg.] C 8h baked heat insulation air-cooling, for the next step step of laying the foundation;

[0036] (3) roughing, finishing, the lathe roughing, the surface of the oxide layer off the car, and precise control of the size, shape finishing producing finished; drilling using drilling drill holes, removing burrs around the hole, allowing drill rod and solder products supporting the use of normal;

[0037] (4) heat treatment process, is heated to a temperature of 960 ± 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Impact toughnessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of production and manufacturing of drilling tool steel, and particularly relates to a heat treatment method of drilling tool steel. According to the method, austenite grains can be fully recovered, recrystallized and refined through reasonable control over deformation temperature and the deformation amount in a forging process, and full preparation is made for improving toughness of steel; and then a cooling rate after forging is controlled, and slow cooling is conducted, so that in a deformation austenite transformation process, proeutectoid ferrite can be fully nucleated and grow up, and necessary conditions are provided for reducing a hardness value of a forging stock. According to the invention, furnace cooling is added after precision forging; and after the furnace cooling, the structure is mainly lath bainite, lath spacing is large, part of grain structure appears, full preparation is made for annealing, and a final blank is obtained after annealing and provided for a user.

Description

technical field [0001] The invention belongs to the technical field of production and manufacture of drill steel, and in particular relates to a heat treatment method for drill steel. Background technique [0002] With the development of society, it is more and more difficult to use in mining, tunnel and other construction, and the requirements are getting higher and higher. In domestic and foreign mining, railway, highway construction, port, power station construction, urban construction, quarrying and other engineering fields A large number of different types of drilling tools are used, and the quality requirements for drilling tools are getting higher and higher. [0003] The heat treatment technology of steel for drilling tools, the mechanical properties, physical performance parameters and quality are one of the key points in the manufacture of drilling tools. Rock drilling tools are used in tension, compression, bending, Under the action of cyclic stress such as torsi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D8/00C21D1/28C21D1/18
CPCC21D8/005C21D1/28C21D1/18
Inventor 尹凤先
Owner CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap