Organic-inorganic montmorillonite composite antibacterial material and preparation method thereof

A technology of compound antibacterial and montmorillonite, applied in the field of antibacterial materials, can solve the problem that Gram-positive bacteria and negative bacteria cannot show good resistance and other problems

Pending Publication Date: 2022-03-25
CHINA UNIV OF MINING & TECH (BEIJING)
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, antibacterial materials mainly use montmorillonite as a carrier, but the existing antibac

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic-inorganic montmorillonite composite antibacterial material and preparation method thereof
  • Organic-inorganic montmorillonite composite antibacterial material and preparation method thereof
  • Organic-inorganic montmorillonite composite antibacterial material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] The invention provides a kind of preparation method of organic-inorganic montmorillonite composite antibacterial material, comprising the following steps:

[0021] (1) activating after mixing the montmorillonite concentrate with water and an acidic solution, to obtain acid leaching montmorillonite;

[0022] (2) the acid-leached montmorillonite obtained in the step (1) is mixed with water to obtain a montmorillonite dispersion;

[0023] (3) The montmorillonite dispersion liquid obtained in the step (2) is mixed with cetylpyridine and copper chloride and then loaded to obtain an organic-inorganic montmorillonite composite antibacterial material.

[0024] In the invention, the montmorillonite concentrate is mixed with water and an acidic solution, and then activated to obtain the acid-leached montmorillonite. The present invention carries out activation treatment to montmorillonite, makes montmorillonite undergo acidification reaction in acidic solution, makes silicon, ir...

Embodiment 1

[0058] The preparation method of organic-inorganic montmorillonite composite antibacterial material is composed of the following steps:

[0059] (1) Mix 5g of montmorillonite concentrate (montmorillonite content greater than 90%) with 250mL of distilled water to obtain a slurry; wherein, the mass ratio of montmorillonite concentrate to distilled water is 1:50;

[0060] (2) Mix the pulp obtained in the step (1) with 0.1mol / L hydrochloric acid solution, activate it at 95°C for 5h, filter it, wash it with distilled water until the pH of the washing solution is 7, and dry it at 60°C to obtain Acid leaching montmorillonite; wherein, the volume ratio of pulp to hydrochloric acid solution is 5:1;

[0061] (3) 2g acid-leached montmorillonite obtained in said step (2) is mixed with 100mL distilled water under ultrasonic stirring conditions to obtain a montmorillonite dispersion; wherein the mass ratio of acid-leached montmorillonite to distilled water is 1: 50, the stirring speed duri...

Embodiment 2

[0064] The preparation method of organic-inorganic montmorillonite composite antibacterial material is composed of the following steps:

[0065] (1) Mix 5g of montmorillonite concentrate (montmorillonite content greater than 90%) with 250mL of distilled water to obtain a slurry; wherein, the mass ratio of montmorillonite concentrate to distilled water is 1:50;

[0066] (2) Mix the pulp obtained in the step (1) with 0.2mol / L hydrochloric acid solution, activate it at 95°C for 5h, filter it, wash it with distilled water until the pH of the washing solution is 7, and dry it at 60°C to obtain Acid leaching montmorillonite; wherein, the volume ratio of pulp to hydrochloric acid solution is 5:1;

[0067] (3) 2g acid-leached montmorillonite obtained in said step (2) is mixed with 100mL distilled water under ultrasonic stirring conditions to obtain a montmorillonite dispersion; wherein the mass ratio of acid-leached montmorillonite to distilled water is 1: 50, the stirring speed duri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of an organic-inorganic montmorillonite composite antibacterial material, which comprises the following steps: mixing montmorillonite concentrate with water and an acidic solution, and activating to obtain acid-leached montmorillonite; mixing the acid-leached montmorillonite with water to obtain a montmorillonite dispersion liquid; and mixing the montmorillonite dispersion liquid with cetylpyridine and copper chloride, and carrying out loading to obtain the organic-inorganic montmorillonite composite antibacterial material. According to the invention, the acid-leached montmorillonite is taken as a carrier, and the structure and layer charge of the montmorillonite are changed through acid leaching treatment, so that the antibacterial property of the material is effectively improved; the acid-leached montmorillonite is mixed with water, so that the acid-leached montmorillonite can be uniformly dispersed in a solution, and the subsequent loading of an organic antibacterial agent cetylpyridine and an inorganic antibacterial agent copper chloride is facilitated, so that the broad-spectrum performance of the antibacterial material is realized, and the antibacterial material can simultaneously show good resistance to gram-positive bacteria and gram-negative bacteria.

Description

technical field [0001] The invention belongs to the technical field of antibacterial materials, and in particular relates to an organic-inorganic montmorillonite composite antibacterial material and a preparation method thereof. Background technique [0002] Antibacterial agents with bactericidal and antibacterial functions are considered to be effective substitutes for antibiotics. They can produce antibacterial active components to achieve antibacterial effects and are not easy to make bacteria resistant. Compared with traditional physical and chemical antibacterial methods The antibacterial method of using antibacterial agents also has the characteristics of strong applicability, small irritation, mild effect, and is not easy to cause allergic reactions. When used, it is usually necessary to load antibacterial agents on the carrier to improve its dispersibility, stability, performance and safety. [0003] At present, antibacterial materials mainly use montmorillonite as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A01N59/20A01N43/40A01N25/08A01P1/00A61K31/4425A61K33/34A61K47/02A61P31/04
CPCA01N59/20A01N43/40A01N25/08A61K31/4425A61K33/34A61K47/02A61P31/04A61K2300/00
Inventor 孙志明郑水林李盛平张晓雨
Owner CHINA UNIV OF MINING & TECH (BEIJING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap