Antiskid plastic woven cloth and preparation method thereof

A plastic woven fabric and anti-slip technology, which is applied in non-woven fabrics, chemical instruments and methods, textiles, etc., can solve the problem of difficult balance between the anti-slip effect and service life of woven fabrics, and achieve good mechanical properties, good anti-slip, and long-term cost Effect

Active Publication Date: 2022-05-13
保定龙军建材有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention proposes a non-slip plastic woven cloth and its preparation method, which solves the problem that the anti-slip effect and service life of the woven cloth are difficult to balance in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A preparation method of non-slip plastic woven cloth, comprising the following steps:

[0032] S00: material preparation

[0033] The non-woven fabric layer comprises the following components by weight:

[0034] 40 parts of homopolypropylene, 20 parts of tackifying masterbatch, 10 parts of high pressure polyethylene, 3 parts of anti-aging masterbatch, 4 parts of color masterbatch;

[0035] The anti-slip film layer includes the following components by weight: 20 parts of high-pressure ethylene, 45 parts of polypropylene, 35 parts of tackifier masterbatch, and 4 parts of double-resistant masterbatch;

[0036] The woven fabric layer is woven with warp and weft threads, and the warp threads include the following components by weight: 50 parts of homopolypropylene, 15 parts of high-pressure polyethylene, 5 parts of ultrafine calcium carbonate, 3 parts of anti-aging masterbatch, 2 parts of turpentine 1 part, 4 parts of color masterbatch, and 1 part of coupling agent; wherei...

Embodiment 2

[0048] A preparation method of non-slip plastic woven cloth, comprising the following steps:

[0049] S00: material preparation

[0050] The parts by weight of each composition of the nonwoven fabric layer are as follows:

[0051] 60 parts of homopolypropylene, 30 parts of tackifying masterbatch, 25 parts of high-pressure polyethylene, 5 parts of anti-aging masterbatch, and 6 parts of color masterbatch;

[0052] The anti-slip film layer includes the following components by weight: 20 parts of high-pressure ethylene, 45 parts of polypropylene, 35 parts of tackifier masterbatch, and 4 parts of double-resistant masterbatch;

[0053] The woven fabric layer is woven with warp and weft threads, and the warp threads include the following components by weight: 70 parts of homopolypropylene, 25 parts of high-pressure polyethylene, 10 parts of ultrafine calcium carbonate, 5 parts of anti-aging masterbatch and 5 parts of turpentine , 6 parts of color masterbatch, 2 parts of coupling ag...

Embodiment 3

[0065] A preparation method of non-slip plastic woven cloth, comprising the following steps:

[0066] S00: material preparation

[0067] The parts by weight of each composition of the nonwoven fabric layer are as follows:

[0068] 51 parts of homopolypropylene, 24 parts of tackifier masterbatch, 17 parts of high pressure polyethylene, 4.2 parts of anti-aging masterbatch, 5.2 parts of color masterbatch;

[0069] The anti-slip film layer includes the following components by weight: 20 parts of high-pressure ethylene, 45 parts of polypropylene, 35 parts of tackifier masterbatch, and 4 parts of double-resistant masterbatch;

[0070] The woven fabric layer is woven with warp and weft threads, and the warp threads include the following components by weight: 60 parts of homopolypropylene, 20 parts of high-pressure polyethylene, 7 parts of ultrafine calcium carbonate, 3.5 parts of anti-aging masterbatch, 3 parts of turpentine 5 parts, 5 parts of color masterbatch, 0.6 parts of coupl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of plastic woven fabrics, and provides an anti-skid plastic woven fabric and a preparation method thereof.The anti-skid plastic woven fabric comprises an anti-skid film layer, a non-woven fabric layer and a woven fabric layer, the non-woven fabric layer is located between the anti-skid film layer and the woven fabric layer, and the woven fabric layer comprises warp and weft which are woven in a staggered mode; the warp is prepared from, by weight, 50-70 parts of homo-polypropylene, 15-25 parts of high-pressure polyethylene, 5-10 parts of superfine calcium carbonate, 3-5 parts of anti-aging master batch, 2-5 parts of turpentine, 4-6 parts of color master batch and 1-2 parts of coupling agent. The wefts are prepared from the following components in parts by weight: 50 to 70 parts of homo-polypropylene, 15 to 25 parts of high-pressure polyethylene, 10 to 20 parts of ethylene-vinyl acetate copolymer, 10 to 15 parts of polyolefin elastomer, 10 to 15 parts of tackifying modified resin and 3 to 8 parts of wear-resistant agent. According to the technical scheme, the problem that in the prior art, the anti-skid effect and the service life of woven cloth are difficult to consider at the same time is solved.

Description

technical field [0001] The invention relates to the technical field of plastic woven cloth, in particular to an anti-slip plastic woven cloth and a preparation method thereof. Background technique [0002] Currently widely used polyolefin plastic woven cloth is usually made of polyethylene or polypropylene, but its surface is smooth and its anti-slip performance is poor, so the performance of its products is greatly limited during the application process. When used as packaging materials For example, after the woven bag is loaded, it is easy to slip during the process of transportation, handling, or storage and stacking, causing certain safety hazards, and it is impossible to increase the stacking height, resulting in a large area of ​​space waste; In the scenario where the slope is slippery but the application environment is relatively harsh, the existing plastic woven cloth cannot meet the dual guarantees of life and safety. [0003] In the prior art, people are also tryi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/02B32B27/32B32B27/06B32B27/18B32B33/00B32B37/08D03D15/283D03D15/292D03D15/37D03D15/50D03D15/573D03D15/58D04H1/4291D04H3/007
CPCB32B5/022B32B5/026B32B5/26B32B33/00B32B37/08D03D15/283D03D15/292D03D15/37D03D15/50D03D15/573D03D15/58D04H1/4291D04H3/007B32B2262/0253B32B2307/554B32B2307/50B32B2307/744B32B2255/02B32B2255/26D10B2321/021D10B2321/022D10B2505/10
Inventor 尤文军
Owner 保定龙军建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com