Electrochemical device and electronic device
An electrochemical and discharge capacity technology, applied in the field of electrochemical energy storage, can solve problems such as unsatisfactory
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0071] Example 1
[0072] Preparation of positive electrode: Lithium cobaltate, conductive carbon black (Super P), and polyvinylidene fluoride (PVDF) were mixed in a weight ratio of 97.5:1.0:1.5, and N-methylpyrrolidone (NMP) was added as a solvent, and stirred evenly . The slurry is uniformly coated on the positive electrode current collector aluminum foil with a coating thickness of 80 μm, and the positive electrode is obtained after drying, cold pressing and cutting.
[0073] Preparation of negative electrode: dissolving epoxy resin in ethanol and stirring for a period of time to obtain a mixed solution, then adding a curing agent (m-phenylenediamine) (epoxy resin: curing agent mass ratio = 10:1) and transferring the mixed solution to a hydrothermal reaction In the kettle, the hydrothermal reaction was carried out under the condition of 180°C, and the solid part was taken out after the temperature was cooled down. It was placed in a box furnace, heated to 200°C for 1 h at...
PUM
Property | Measurement | Unit |
---|---|---|
Adhesion | aaaaa | aaaaa |
Compaction density | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap