Mineral modified polypropylene composite material for vehicles and preparation method of mineral modified polypropylene composite material

A composite material and polypropylene technology, which is applied in the field of mineral modified polypropylene composite materials for vehicles and its preparation, can solve the problems of high cost, difficult processing of composite materials, complex formula composition and other problems, and achieve cost controllable , achieve balance and aging resistance, and the effect of large market competitive advantages

Pending Publication Date: 2022-07-08
SUZHOU SUNWAY POLYMER
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are many types of PP modified materials of various grades on the market, the composite materials are not easy to process or the appearance of the products is poor due to fillings such as minerals and glass fibers, and many modified PP materials have complex formulas, making it difficult to take care of various types. Balance of performance; PP modified materials that can balance ordinary mechanical properties and have good aging resistance are relatively few, or a good balance of properties has been obtained, but the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mineral modified polypropylene composite material for vehicles and preparation method of mineral modified polypropylene composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A mineral-modified polypropylene composite material for vehicles is prepared from the following raw materials in parts by weight: 72 parts of copolymerized polypropylene, 26 parts of talc masterbatch, 2 parts of ethylene-octene toughening agent, 0.25 part of stabilizer, 0.15 part lubricant and 0.5 part antioxidant.

[0039] Its specific preparation method is as follows:

[0040] S1. Preparation of talc masterbatch: weigh 30 parts of PP resin and 70 parts of talc powder by weight, put them into a twin-screw extruder for mixing, the temperature of each zone of the screw is 180°C, the screw speed is 450 rpm, and the mixing After refining, extrude and granulate to obtain talc master batch, which is cooled for later use.

[0041] S2, material preparation: weigh each raw material and the talc master batch prepared in S1 one by one according to the formula weight ratio, and set aside.

[0042] S3. Premix: Mix the copolymerized polypropylene, toughening agent and talc masterb...

Embodiment 2

[0045] A mineral-modified polypropylene composite material for vehicles is prepared from the following parts by weight of raw materials: 68 parts of copolymerized polypropylene, 30 parts of talc masterbatch, 2 parts of ethylene-octene toughening agent, 0.25 part of stabilizer, 0.15 part lubricant and 0.5 part antioxidant.

[0046] Its specific preparation method is as follows:

[0047] S1. Preparation of talc masterbatch: weigh 30 parts of PP resin and 70 parts of talc powder by weight, put them into a twin-screw extruder for mixing, the temperature of each zone of the screw is 180°C, the screw speed is 450 rpm, and the mixing After refining, extrude and granulate to obtain talc master batch, which is cooled for later use.

[0048] S2, material preparation: weigh each raw material and the talc master batch prepared in S1 one by one according to the formula weight ratio, and set aside.

[0049] S3. Premix: Mix the copolymerized polypropylene, toughening agent and talc masterbat...

Embodiment 3

[0052] A mineral-modified polypropylene composite material for vehicles is prepared from the following raw materials in parts by weight: 72 parts of copolymerized polypropylene, 26 parts of talc masterbatch, 4 parts of ethylene-octene toughening agent, 0.25 part of stabilizer, 0.15 part lubricant and 0.5 part antioxidant.

[0053] Its specific preparation method is as follows:

[0054] S1. Preparation of talc masterbatch: weigh 30 parts of PP resin and 70 parts of talc powder by weight, put them into a twin-screw extruder for mixing, the temperature of each zone of the screw is 180°C, the screw speed is 450 rpm, and the mixing After refining, extrude and granulate to obtain talc master batch, which is cooled for later use.

[0055] S2, material preparation: weigh each raw material and the talc master batch prepared in S1 one by one according to the formula weight ratio, and set aside.

[0056] S3. Premix: Mix the copolymerized polypropylene, toughening agent and talc masterb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a mineral modified polypropylene composite material for vehicles and a preparation method thereof, and provides the following technical scheme aiming at the problems of the existing PP modified material: the mineral modified polypropylene composite material is prepared from the following raw materials in parts by weight: 50-90 parts of polypropylene (PP), 10-40 parts of talc master batch, 3-10 parts of flexibilizer, 0.1-0.5 part of stabilizer, 0.1-0.5 part of lubricant and 0.2-1 part of other auxiliaries. The preparation method comprises the following steps: material preparation, material premixing and mixing. The mineral modified polypropylene composite material for vehicles provided by the invention has good mechanical properties and excellent aging resistance, and also has good processability and product appearance, and the preparation method of the material provided by the invention is simple and has high comprehensive benefits.

Description

technical field [0001] The invention relates to the field of polypropylene modified materials, more particularly, to a mineral modified polypropylene composite material for vehicles and a preparation method thereof. Background technique [0002] With the development of the automobile industry, more and more automobile parts choose modified engineering plastics to replace metal parts, and more and more plastic varieties can be applied, such as PP (polypropylene), PA (nylon), ABS ( polyacrylonitrile-butadiene-styrene), PBT (polybutylene terephthalate), PET (polyethylene terephthalate), and the like. The application of plastics in automobiles has been developing for more than half a century, which has greatly promoted the lightweight development of automobiles, promoted energy conservation and emission reduction, and provided drivers with a good driving experience and riding comfort. [0003] In the development and application of many automotive plastics, PP materials have bee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L23/10C08L23/08C08K3/34C08J3/22
CPCC08L23/14C08J3/226C08J2323/14C08J2423/10C08J2423/08C08K3/34C08L23/10C08L23/0815
Inventor 王彬刘少峰李维旋
Owner SUZHOU SUNWAY POLYMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com