Irreversible temperature change ceramic tile composite board

A composite board and ceramic tile technology, applied in covering/lining, construction, ink, etc., can solve the problems of increasing labor and material resources, inconsistent thermal expansion coefficient, plate deformation, etc., to reduce labor and material costs, improve construction efficiency, reduce The effect of the test work

Active Publication Date: 2022-07-29
ZHEJIANG YASHA DECORATION
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the thermal expansion coefficients of the tiles of the tile composite board and the wall panel substrate are inconsistent, and when the two are placed in an environment exceeding 50°C, they will be deformed or even warped.
The storage environment of the composite board after the completion of the factory is controllable, but during the transportation process, due to the difference in temperature between the north and the south, as well as various emergencies during transportation, the composite board may experience a high temperature environment exceeding 50°C, resulting in deformed
After the ceramic tile composite panels are transported to the construction site, in order to confirm whether the composite panels are deformed, the on-site construction personnel need to measure each composite panel, which seriously affects the efficiency of on-site construction, and also significantly increases the expenditure of manpower and material resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An irreversible thermochromic ceramic tile composite board, the ceramic tile composite board includes a base plate and a ceramic tile compounded on the base plate; wherein, an irreversible thermochromic layer is arranged on the side of the ceramic tile, and the irreversible thermochromic layer is composed of an irreversible thermochromic layer. The color-changing ink is cured and formed. It is prepared by the following steps:

[0028] (1) Take a 600mm*2440mm conventional stone-plastic board as the substrate, apply two-component polyurethane glue on the surface of the substrate, and open it for 10-15min; then compound a 600mm*600mm conventional tile on the substrate, so that the tile and the substrate are connected. Closely fit between each other to obtain a tile composite board with four tiles on a large board.

[0029] (2) In parts by mass, add 60 parts of photocurable diluent (25 parts of HDDA, 35 parts of TPGDA), 60 parts of prepolymer (CN959), and 6 parts of photos...

Embodiment 2

[0032] An irreversible thermochromic ceramic tile composite board, the ceramic tile composite board includes a base plate and a ceramic tile compounded on the base plate; wherein, an irreversible thermochromic layer is arranged on the side of the ceramic tile, and the irreversible thermochromic layer is composed of an irreversible thermochromic layer. The color-changing ink is cured and formed. It is prepared by the following steps:

[0033] (1) Take a 600mm*2440mm conventional stone-plastic board as the substrate, apply two-component polyurethane glue on the surface of the substrate, and open it for 10-15min; then compound a 600mm*600mm conventional tile on the substrate, so that the tile and the substrate are connected. Closely fit between each other to obtain a tile composite board with four tiles on a large board.

[0034] (2) In parts by mass, add 20 parts of light-curing diluent (10 parts of HEMA, 10 parts of TPGDA), 40 parts of prepolymer (20 parts of CN959, 20 parts o...

Embodiment 3

[0037] An irreversible thermochromic ceramic tile composite board, the ceramic tile composite board includes a base plate and a ceramic tile compounded on the base plate; wherein, an irreversible thermochromic layer is arranged on the side of the ceramic tile, and the irreversible thermochromic layer is composed of an irreversible thermochromic layer. The color-changing ink is cured and formed. It is prepared by the following steps:

[0038] (1) Take a 600mm*2440mm conventional stone-plastic board as the substrate, apply two-component polyurethane glue on the surface of the substrate, and open it for 10-15min; then compound a 600mm*600mm conventional tile on the substrate, so that the tile and the substrate are connected. Closely fit between each other to obtain a tile composite board with four tiles on a large board.

[0039] (2) In parts by mass, add 25 parts of photocurable diluent (10 parts of TMPTA, 15 parts of TPGDA), 55 parts of prepolymer (35 parts of CN959, 20 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of composite boards, and particularly relates to an irreversible temperature change ceramic tile composite board. The ceramic tile composite board comprises a base board and ceramic tiles compounded on the base board, wherein an irreversible thermochromic layer is arranged on the outer side surface of the ceramic tile, and the irreversible thermochromic layer is formed by curing irreversible thermochromic ink. The irreversible thermochromic layer is arranged on the outer side face of the ceramic tile composite board, when the ceramic tile composite board experiences the environment temperature larger than or equal to 50 DEG C in the transportation process, the composite board can irreversibly deform, meanwhile, the irreversible thermochromic layer can also irreversibly change in color, and when the composite board is transported to a construction site from a factory, the irreversible thermochromic layer can change color irreversibly. A worker can simply judge whether the composite board deforms or not in the transportation process according to the color change of the side face of the composite board, so that the test work on the composite board on site is reduced, the site construction efficiency is improved, and the expenditure of manpower and material resources is reduced.

Description

technical field [0001] The invention belongs to the field of composite boards, in particular to an irreversible temperature-changeable ceramic tile composite board. Background technique [0002] With the development of modern industrial technology, building houses can be manufactured in batches like machine production. It is only necessary to transport the prefabricated building components to the construction site for assembly. Industrial prefabricated buildings are fast in construction and low in production cost, and are increasingly used in modern architectural decoration. [0003] The ceramic tile composite panel is a part of the industrialized assembly module, which is formed by pre-fitting tiles of a fixed size on a large wall panel, which is referred to as a wall composite panel. The construction site can directly form a complete wall by connecting the composite panels through structural parts according to the requirements, eliminating the need for gluing, tiling, ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/14C09D11/101C09D11/03
CPCE04F13/142C09D11/101C09D11/03
Inventor 丁欣欣王文广郑坚周东珊胡耀清彭伟
Owner ZHEJIANG YASHA DECORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com