Biological wave ceramic material for human body sha-syndrome scraping plate and its preparing method

A technology of ceramic materials and biological waves, applied in the field of ceramic materials, can solve the problems of failing to regulate the human biological information field, microvascular rupture, and slow recovery from fever.

Inactive Publication Date: 2002-06-05
TSINGHUA UNIV
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the traditional scraping board does not have the function of far-infrared wave radiation, when it contacts with human skin, it cannot emit waves similar to the human biological wave spectrum and produce resonance absorption to absorb human energy, which cannot achieve the effect of regulating the human biological information field. It is only required that there is no adverse reaction when it comes into contact with human skin
Scraping with traditional scraping board requires a lot of force, which can easily cause microvascular rupture, and is easy to be infected with blood-borne diseases.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biological wave ceramic material for human body sha-syndrome scraping plate and its preparing method
  • Biological wave ceramic material for human body sha-syndrome scraping plate and its preparing method
  • Biological wave ceramic material for human body sha-syndrome scraping plate and its preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 500 g Fe 2 o 3 , 300 grams of MgO, 195 grams of ZnO, 5 grams of CaO, (a total of 1000 grams) ball milled in a silicon carbide grinding tank with an appropriate amount of deionized water for 30 hours, and then dried the material; put the powder into the electric kiln with a bowl Pre-firing, the kiln is 9 meters long, the middle constant temperature zone is 2 meters, the temperature in the constant temperature zone is 950°C, the propulsion speed of the bowl is 1 m / hour, and the temperature of the furnace is <200°C; the pre-fired powder is added with an appropriate amount of deionized water ball mill for 18 Hours, dry; add 0.8wt% polyvinyl alcohol binder and appropriate amount of deionized water to the dried powder, mix evenly to make the dilution moderate, use spray granulator to granulate, spherical particle size 30-80μm; then molded with a mold, the molding pressure is 20Mpa, the surface of the green body is bright, and has a certain mechanical strength; after the gree...

Embodiment 2

[0025] 403 g Fe 2 o 3 , 340 grams of MgO, 250 grams of ZnO, 7 grams of CaO, (a total of 1000 grams) ball milled in a silicon carbide grinding tank with an appropriate amount of deionized water for 30 hours, and then dried the material; put the powder into the electric kiln with a bowl Pre-firing, the kiln is 9 meters long, the middle constant temperature zone is 2 meters, the temperature in the constant temperature zone is 900 ° C, the bowl propulsion speed is 1 m / hour, and the furnace temperature is < 200 ° C; the pre-fired powder is added with an appropriate amount of deionized water ball mill for 18 Hours, dry; add 0.6wt% polyvinyl alcohol binder and appropriate amount of deionized water to the dried powder, mix evenly to make the dilution moderate, use spray granulator to granulate, spherical particle size 30-80μm; then molded with a mold, the molding pressure is 18Mpa, the surface of the green body is bright, and has a certain mechanical strength; after the green body ...

Embodiment 3

[0026] 600 g Fe 2 o 3 , 240 grams of MgO, 157 grams of ZnO, 3 grams of CaO, (a total of 1000 grams) ball milled in a silicon carbide grinding tank with an appropriate amount of deionized water for 30 hours, and then dried the material; put the powder into the electric kiln with a bowl Pre-firing, the kiln is 9 meters long, the middle constant temperature zone is 2 meters, the temperature in the constant temperature zone is 980°C, the propulsion speed of the bowl is 1m / hour, and the furnace temperature is <200°C; the pre-fired powder is added with an appropriate amount of deionized water ball mill for 18 Hours, dry; add 0.9wt% polyvinyl alcohol binder and appropriate amount of deionized water to the dried powder, mix evenly to make the dilution moderate, use spray granulator to granulate, spherical particle size 30-80μm; then molded with a mold, the molding pressure is 21Mpa, the surface of the green body is bright, and has a certain mechanical strength; after the green body i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
emissivityaaaaaaaaaa
Login to View More

Abstract

A biological wave ceramic material for making sha-syndrome scraping plate has in its formula Fe2O3 40-60 wt%, MgO 24-34 wt%, ZnO 15-25 wt% and CaO 0.3-7 wt% as well as small amount of adhesive. the biological wave ceramic material is prepared from the above-mentioned ingredients through mixing, grinding, stoving, pre-sintering at 900-1000 deg.c, re-grinding, stoving, pelletizing, molding for shaping, sintering at 1100-1300 deg.C and polishing. The said mold has one concave arc-shape side, one wavy or linear side and two wedged short sides. The Sha-syndrome scraping plate of the present invention can radiate far infrared wave with biological wave spectrum similar to that of human body, can regulate human body's biological information field and will not produce break of capillary blood vessel white it is used to scrape on the body.

Description

technical field [0001] The invention relates to a biological wave ceramic material for human body scraping plates and a preparation method thereof, belonging to the technical field of ceramic materials. Background technique [0002] Scraping is a part of traditional Chinese medicine. In clinical practice, scraping is to scrape along the meridians to promote its conduction and transport of qi and blood, adjust the functions of meridians and viscera, and restore the pathological changes of the human body to normal physiological functions. The usual equipment used for scraping is a hand-held sheet made of metal, animal bone or organic material, that is, a scraping board. Because the traditional scraping board does not have the function of far-infrared wave radiation, when it contacts with human skin, it cannot emit waves similar to the human biological wave spectrum and produce resonance absorption to absorb human energy, which cannot achieve the effect of regulating the human ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61H7/00C04B35/26C04B35/622C04B35/632
Inventor 张宝清田杰谟王止文林旭平李有红魏书炳
Owner TSINGHUA UNIV