Artist clay material and production thereof

A production process and technology, applied in the field of new craft clay materials, to achieve the effect of bright color, easy preparation, and not easy to break

Inactive Publication Date: 2004-07-07
SANHE SCI & TECH COOP SHANGHAI
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is: to change various defects of traditional craft clay materials, and disclose a new craft clay material (referred to as soft pottery material), which has strong plasticity, bright color, will not fall off, and will not dry in a cool place at room temperature. , the curing temperature is not high, the process is easy to realize

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Artist clay material and production thereof
  • Artist clay material and production thereof
  • Artist clay material and production thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The formula ratio of the new clay material is selected as:

[0012] PVC powder resin: 45; dioctyl ester: 17; plastic: 4; calcium carbonate: 34.

[0013] Toners imported from the UK are used as coloring additives, mixed with different colors, and molded into bear toys, and then baked in an electric oven at 130°C for less than 30 minutes. After drying and hardening, it becomes a soft clay toy with bright colors and novel shapes.

Embodiment 2

[0015] The formula ratio of the new clay material is selected as:

[0016] PVC powder resin: 43; dioctyl ester: 20; plastic: 2; calcium carbonate: 35.

[0017] Match it with different colors, shape it into a penguin toy, and then put it in an electric oven and bake it at 140°C for less than 30 minutes. After drying and hardening, it becomes a soft clay toy with eye-catching colors and innovative shapes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An artistical clay material is prepared from powdered PVC resin (43-45%), dioctylester (15-20), plastics (2-5) and calcium carbonate (32-35). Its artwork can be calcined at 130-140 deg.C for less than 30 min, and features low calcine temp. gay color and high firmness.

Description

1. Technical field: [0001] The invention relates to a craft clay material, and in particular discloses a novel craft clay material, which is used in the industry of shaping handicrafts. 2. Background technology: [0002] Traditional clay handicraft materials mainly include plasticine, kaolin, clay and gypsum. Plasticine is very familiar to people and has strong plasticity, but it has the disadvantage of not being able to shape; both kaolin and clay need to be fired in a high-temperature room to be shaped and solidified, and certain conditions are required for shaping, and the color is less, or glazed and colored, and Weaknesses such as easy breakage; gypsum can be cured at low temperature, but the color is less, most of which are white, and the material is brittle and easy to break. 3. Contents of the invention: [0003] The technical problem to be solved by the present invention is: to change various defects of traditional craft clay materials, and disclose a new craft c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K5/10C08L27/06
Inventor 马峻
Owner SANHE SCI & TECH COOP SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com