Iron-cobalt alloy nano linear array permanent-magnetic film material and its preparation

A nanowire array, iron-cobalt alloy technology, applied in the application of magnetic films to substrates, and the magnetism of inorganic materials, can solve the problems of ignoring permanent magnetic film materials

Inactive Publication Date: 2004-09-15
NANJING UNIV
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the research on permanent magnet thin film materials such as rare earth permanent magnets, transition metal permanent magnets and ferrite permanent magnets mentione

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Iron-cobalt alloy nano linear array permanent-magnetic film material and its preparation
  • Iron-cobalt alloy nano linear array permanent-magnetic film material and its preparation
  • Iron-cobalt alloy nano linear array permanent-magnetic film material and its preparation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] Below in conjunction with accompanying drawing and by embodiment the present invention will be further described:

[0013] Iron-cobalt alloy Co x Fe 1-x (0.20≤x≤0.60) formula has a certain range, and the present invention is especially formulated in the range of 0.25≤x≤0.40, the ratio of performance and cost of this ratio is the most economical, and there is no significant difference in performance.

[0014] The invention is manufactured by the following method: the aluminum oxide nano hole template is prepared by electrochemical anodic oxidation, the electrolytic solution is 2%-15% sulfuric acid aqueous solution, the voltage is 10V-27V, and phosphoric acid is used to expand the pores. Using nanoporous alumina as a template, the electrodeposition solution is an aqueous solution containing iron ions and cobalt ions, and Co is obtained by alternating current electrochemical deposition. x Fe 1-x (0.20≤x≤0.60) alloy nanowire arrays followed by annealing. The electrodepo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

In the invention, pore templet in Nano alumina is prepared by method of electrochemic anode oxidation, and nano line array of ferrocobalt is prepared by method of electrochemic deposition. Diameter of line array of ferrocobalt is in 10nm-50nm, constituent of ferrocobalt is as CoxFe1-x , 20 more than or equal to 20 and less than or equal to 0.60. low temperature annealing of Nano line array of ferrocobalt obtained from electrochemic deposition obtains thin film material of permanent magnetism, performances of which are best when content of cobalt is 30%-40%, and diameter of Nano line is as 10nm-22nm.

Description

1. Technical field [0001] The invention relates to a composition and a preparation method of an iron-cobalt alloy nanowire array permanent magnet thin film material. 2. Background technology [0002] Permanent magnetic thin films can be widely used in micro-motor systems, integrated electronic devices, magnetic heads and other fields, and use permanent magnetic thin films to form micro-motors, braking devices, micro-pumps and other devices. With the miniaturization of electronic devices, research on permanent magnetic thin films has received widespread attention and developed rapidly. The selection criteria for permanent magnetic films are 1) good magnetic properties: large magnetic energy product, high Curie temperature, H c and B r Has a low temperature coefficient. 2) It can be obtained by sputtering deposition and chemical deposition, and finally can be obtained by chemical deposition. 3) It has good environmental stability: good mechanical properties and oxidation r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01F1/04H01F41/14
Inventor 唐少龙陈微姬广斌李震都有为
Owner NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap