Polytrimethylene terephthalate, and its production and ptt fibre produced with the same

A technology of polytrimethylene terephthalate and its production method, which is applied in the field of PTT fiber and can solve the problems of poor spinning efficiency and the like

Active Publication Date: 2005-07-13
HYOSUNG CORP
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the case of using PTT with a number average molecular weight of 17,000 and a polydispersity index of 2.9 to produce fibers, the tenacity of the fibers was less than 3.5 g / d, and the spinning efficiency of PTT was poor compared to polyester produced by conventional methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polytrimethylene terephthalate, and its production and ptt fibre produced with the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3 and comparative Embodiment 1-2

[0042] Add 300kg of polytrimethylene terephthalate resin to a volume of 1m 3 in the reactor. It was then processed under conditions as indicated in Table 1. The physical properties of the polytrimethylene terephthalate resin were measured before and after the treatment, and the results are shown in Table 1.

Embodiment 4

[0044] The resin treated according to Example 1 was subjected to a spinning drawing process to produce a raw yarn.

[0045] At this time, the spinning drawing process is performed under predetermined conditions including: a single fiber fineness of at least 1 denier, a speed of at least 3,000 m / min, a cooling air flow rate of 0.3 m / sec, and oil The stickiness was 0.7% by weight. Also, PTT is stretched and then heat set.

[0046] The first stretching temperature is 60-80°C, and the second stretching temperature is 110-170°C. In addition, the obtained PTT fiber had a tenacity of 4.1 g / d and an elongation of 31%.

[0047] In addition, the package change cycle (pack change cycle) was 7 days before treatment and extended to 14 days after treatment, and the number of yarn breaks during spinning was significantly reduced from 4 times / day to 1 time / day.

[0048]Circular knitting process is performed on PTT fibers using a 32 inch-28 caliber circular knitting machine, and dyed with B...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tenacityaaaaaaaaaa
tenacityaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a PTT resin having a number-average molecular weight of at least 20,000 and a polydispersity index of 1.3-2.7, a method for producing the same, and a PTT fiber produced using the same. The advantage of the PTT resin is that it has a uniform molecular weight distribution, thus suppressing the increase of package pressure, and prolonging the package change cycle and wiping cycle in the spinning process of PTT fibers. Thus, the productivity of the PTT fiber is increased, the regularity ratio of the raw yarn produced using the PTT fiber is increased, and the physical properties of the raw yarn are improved. In addition, because PTT fibers have relatively high tenacity due to their relatively high molecular weight, the inherent and desired physical properties of PTT fibers such as flexibility, elastic recovery, softness, and chemical resistance are difficult to obtain in subsequent processes such as false twisting processes. , stretching process, knitting process and weaving process almost no reduction. Therefore, the processability of the PTT fiber in the subsequent process is improved, and therefore, the production cost of the PTT fiber is reduced regardless of its application, such as for cloth or industrial fibers.

Description

technical field [0001] The present invention relates to polytrimethylene terephthalate (PTT) resin having high toughness, its production method, and PTT fiber produced using the same, said polytrimethylene terephthalate (PTT) resin having at least 20,000 Number average molecular weight (Mn) and polydispersity index (PDI) of 1.3-2.7, polydispersity index indicates the dispersion of molecular weight. Background technique [0002] WO 99 / 11709 discloses a process for producing PTT having an intrinsic viscosity of 0.4-2.0 dl / g using phosphorus compounds and metal compounds as polycondensation solvents. [0003] The present invention has conducted in-depth research on the production of PTT, and found that the number-average molecular weight and polydispersity index of PTT have a greater impact on the quality of PTT than the intrinsic viscosity of PTT. [0004] Generally, PTT produced by conventional methods has a number average molecular weight of 17,000 and a polydispersity inde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/183C08G63/80C08G63/88D01F6/62H04B1/40
CPCC08G63/183C08G63/80C08G63/88D01F6/62C08G63/78
Inventor 金圣柱孙亮国权益铉
Owner HYOSUNG CORP