A chemical grouting and high-viscosity technology, applied in shipbuilding, ship design, ships, etc., can solve the problems of reduced grouting strength, inability to fully restore appearance, inability to function as a filler, etc.
Inactive Publication Date: 2005-11-30
郭尚运
View PDF0 Cites 9 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, since the sodium silicate added as a filler has a high adsorption force to the resin, the chemical grouting with epoxy resin as the main component has the problem that the sodium silicate filler is not uniformly dispersed and thus cannot function as a filler, and the grouting The strength of the crack is reduced, and the adhesion between the cracks is reduced so that the crack occurs again
[0011] Also, when conventional grouts containing epoxy and sodium silicate are injected into cracks, the grout may not be easily injected due to the presence of air bubbles in the cracks
In particular, in the case of narrow pipe or crack widths, the injection of grout is severely blocked by air bubbles
and the grout is either adsorbed to the parent building or cured and shrinks so it cannot completely fill in the cracks
[0012] In addition, traditional repair and reinforcement methods for buildings are complicated, and it takes a long time before the building is restored to normal after repair, the damaged appearance cannot be fully restored, and cracks often regenerate
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0064] Example 1: Preparation of non-shrinkage high-viscosity chemical grout
[0065] 1kg epoxy liquid phase resin (YD-128 of Kuk-do chemical company) is mixed with 20g ethanol, to which adding 1kg average particle diameter is 1 millimeter glass beads (Jisan Industry) and 500g average particle diameter is 200 mesh and Glass powder (Kumyoong Industry) with a specific gravity of 2.54, which were mixed in an ordinary mixer to prepare non-shrinking high-viscosity chemical grout.
[0066] The non-shrinkage high viscosity chemical grout prepared had a specific gravity of 1.3 and a fluidity of 50 cm as a result of the slump test. The grout was packed into steel tanks and stored at room temperature for 12 months before being opened. As a result, it was observed that part of the filler was precipitated but not solidified, and the filler was evenly dispersed by shaking the tank.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
| width | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
Login to view more
Abstract
The present invention relates to a non-shrink high viscosity chemical grout composition, more particularly to a non-shrink high viscosity chemical grout composition comprising, on the basis of solid content, a) 100 parts by weight of a room temperature curable organic liquid phase resin; b) 10 to 200 parts by weight of glass beads; and c) 10 to 500 parts by weight of glass powder. In addition, the present invention relates to a method for repairing and reinforcing a construction using the non-shrink high viscosity chemical grout composition. The non-shrink high viscosity chemical grout composition of the present invention has superior acid resistance, alkali resistance, injection property, fluidity, crack resistance, impact resistance, adhesion property and storage property, and the method for repairing and reinforcing a construction of the present invention has affinity with subsidiary materials, can completely restore function and shape of a construction in short time due to rapid curing and simple construction, compensates properties of construction such as tensile strength, allows strong adhesion to a construction, and prolongs lifetime of a construction.
Description
technical field [0001] The invention relates to non-shrinkage high-viscosity chemical grouting, especially non-shrinkage high-viscosity chemical grouting with excellent acid resistance, alkali resistance, injectability, fluidity, impact resistance, crack resistance, adhesion and storage resistance. Also, the present invention relates to methods of repairing and reinforcing buildings using the non-shrinkage high viscosity chemical grout. Background technique [0002] Grouting material is an injection material that is injected into the cracks or cavities of the foundation to obtain the effect of soil reinforcement or water leakage prevention. [0003] The injection material is filled using gravity or a pump, and is used to enhance the supporting force of a shaft portion or a base portion of a building or repair cracks of a building. [0004] According to its construction use, grouting can be divided into water retention grouting, foundation improvement grouting, filling grout...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more Patent Type & Authority Applications(China)
IPC IPC(8): C04B14/22B63B9/00C04B26/14C04B26/16C04B41/48E04G23/02
CPCC04B2111/70C04B41/009C04B41/4853C04B2201/10B63B2231/72C04B26/16C04B2111/34B63B2231/40E04G23/0218C04B2111/74C04B41/4884C04B2111/72B63B9/00E04G23/0203C04B26/14B63B71/00E04G23/0211C04B14/22C04B14/24C04B14/42C04B20/0076C04B14/386
Inventor 郭尚运
Owner 郭尚运
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap