1000Mpa-grade high-strength hot-rolled anti-bullet steel plate and making method

A manufacturing method and high-strength technology, applied in the field of metal materials, can solve the problems of reduced bulletproof performance, low strength, low high plasticity, etc., and achieve the effect of no decline in bulletproof performance and low manufacturing cost

Active Publication Date: 2006-08-09
BAOSHAN IRON & STEEL CO LTD
View PDF1 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The bullet-proof steel of cash transport vehicles is generally not more than 3mm. The steel plate with quenching and low-temperature tempering has high strength and low plasticity, and the plate shape and cold working performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 1000Mpa-grade high-strength hot-rolled anti-bullet steel plate and making method
  • 1000Mpa-grade high-strength hot-rolled anti-bullet steel plate and making method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0048] Table 1 is the chemical composition of the test steel, and Table 2 is the composition of the comparative steel. The steel of the present invention does not contain precious alloying elements such as Cr and Co, and the Mn content is much lower than that of the comparative steel.

[0049] Example

[0050] Comparative example

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

This invention relates to a kind of high strength hot-rolled bulletproof steel of 1000Mpa in the following weight percentage: C 0.17-0.21%, Si 1.5-2.2%, Mn 1.5-2.0%, P<=0.035%, S<=0.010%, Al 0.015-0.060%, N<=0.0060%, Nb 0.010-0.050%, Ti 0.010-0.060%, Ca<=0.0050%, Fe and unavoidable impurities, which is processed in the following steps: a, smelting according to the above mentioned components, casting to form slabs, b, heating the slabs to 1100-1250DEG C, hot-rolling the slabs in the austenitic area and over 80% of them are deformed and the final temperature is 800-900DEG C, d, the final rolled steel is cooled to 650-780DEG C in the speed of 50deg.C/s and air cooled for 6-15 seconds, e, cooling them to 350-450deg.C in the speed over 50deg.C/s, f, rolling them and air cooling them to room temperature.

Description

technical field [0001] The invention belongs to the field of metal materials, in particular to an iron-based alloy containing C, Si, Mn, Nb and Ti. It is a high-strength hot-rolled bulletproof steel plate without heat treatment and a manufacturing method thereof, and the steel plate is especially suitable for being used as a bulletproof material for cash transport vehicles. Background technique [0002] Bulletproof cash transport vehicles and other bulletproof vehicles, such as mobile bank vehicles, private bulletproof cars, police bulletproof patrol vehicles, riot vehicles, riot vehicles, etc., bulletproof is their most basic requirement. In order to achieve the purpose of bulletproof, bulletproof steel plate is generally used as the key material for protection. [0003] The main function of the bulletproof steel plate is to prevent bullets from penetrating the steel plate. Increasing the thickness of the steel plate increases the energy required for the projectile to pene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/12C21D6/00C21D7/13C21D9/46
Inventor 黄镇如马鸣图
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap