Paste type plate manufacturing method and alkaline accumulator using same

A manufacturing method and storage battery technology, applied to alkaline storage batteries, alkaline storage battery electrodes, etc., can solve the problems of decreased storage capacity, increased internal impedance of storage batteries, and shortened tool life

Active Publication Date: 2006-09-06
THE FURUKAWA BATTERY CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, in the punching method described in the above-mentioned publication, the active material layer filled with the active material of the original plate is directly cut, so there is the following problem: the tool life is shortened Short, requires frequent tip grinding or tip replacement, troublesome maintenance
[0009] The method described in the above publication cannot obtain sufficient bonding strength because the end of the pole plate is covered with hot-melt resin in a U-shape
In addition, even if the resin is formed thinly, a gap is generated between the electrode plate and the separator due to the thickness of the resin
[0010] There is a gap between the electrode plate and the separator, which reduces the adhesion between the two, causing the internal impedance of the battery to increase and the battery capacity to decrease

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paste type plate manufacturing method and alkaline accumulator using same
  • Paste type plate manufacturing method and alkaline accumulator using same
  • Paste type plate manufacturing method and alkaline accumulator using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] Embodiments of the present invention will be described in detail below with reference to the accompanying drawings.

[0028] The feature of the present invention is that the part with active matter (active matter) in the cutting part is cut off by a cutting tool (scissors tool), and the part without active matter is punched out by a stamping tool, thereby prolonging the life of the tool and preventing warping of the pole plate section Curved edges and bumps.

[0029] figure 1 A cutting machine (shearing machine) 1 for carrying out the manufacturing method of the present invention is shown. Among them, 11 is a driving device, 12 is an upper cutting tool, 13 is a lower cutting tool, 14 is a pedestal for installing the lower cutting tool 13, 15 is a control device for changing the speed of the driving roller, 16 is a driving roller, and 17 is a conveyor. roll. The paste type electrode plate of the present invention can be applied to either a positive electrode plate or ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention relates to a method for manufacturing a kind of polar plate for alkaline battery, which comprises these processes: prepare the first region by forming reactive layer on porous metal base plate and the second region revealed on the porous metal base plate; blank the polar plate separately with shearing tool on the first region and stamping tool on the second region to obtain polar plate of regular shape.

Description

technical field [0001] The present invention relates to a method for producing a paste-type electrode plate in which a porous metal substrate is filled and coated with an active material, and an alkaline storage battery using the same. Background technique [0002] In recent years, with the rapid development of portable and cordless devices, the batteries for these devices are also increasingly required to be small and lightweight secondary batteries with high energy density. Among them, high-capacity and economical secondary batteries are also required, and alkaline storage batteries represented by nickel-metal hydride storage batteries and nickel-gallium storage batteries are highly desired to reduce the cost and improve reliability in the market. [0003] Alkaline storage batteries such as nickel-gallium storage batteries are manufactured by stacking a plurality of positive and negative plates alternately via separators and placing them in a cell. Gallium, which can be f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/26H01M10/24
CPCY02E60/124Y02E60/10
Inventor 阿部勋叶坂浩一
Owner THE FURUKAWA BATTERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap