Ivory-yellow-padding decorative daily-use fine porcelain

A yellow and ivory technology, which is applied in the field of ceramic products, can solve the problems of porcelain body porcelain clay formula and firing process, difficult control of firing process, difficulty in guaranteeing product quality, uneven color, etc., to ensure color stability, Simple composition and uniform color effect

Inactive Publication Date: 2006-10-25
邯郸臣邦陶瓷有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the traditional porcelain making process, the yellow porcelain body is made by adding different types and different amounts of yellow agents to the body mud, such as vanadium zirconium yellow material, and the glaze is calcareous raw material glaze. The body and glaze are fired at high temperature at the same time. , its color is uneven, opaque, and the ideal color cannot be obtained
In addition, there are still the following technical problems in the firing process of porcelain: the formula of porcelain body porcelain clay, the firing process, and the calcination process are not easy to control, especially some natural raw materials in porcelain clay are unstable, resulting in more color fluctuations at high temperatures. Large, making it difficult to guarantee the quality of the final product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Example 1 Light yellow ivory-yellow tire decorative fine porcelain for daily use

[0014] The composition of matrix porcelain clay is expressed in terms of mass and number: 24 parts of quartz, 13 parts of feldspar, 11 parts of kaolinite powder, 13 parts of washed kaolin, 4 parts of kaolin, 25 parts of kaolinite, 4 parts of clay, and bentonite 3 parts, 4 parts of ivory yellow porcelain body powder, 3 parts of ivory yellow clay, 0.1 part of vanadium zirconium yellow pigment. The ivory yellow body mud mentioned above is the mud made from the above ingredients except the ivory yellow body mud and the ivory yellow porcelain body powder. Porcelain bodies composed of ingredients other than porcelain body powder are obtained by crushing inferior or waste products of porcelain products obtained after firing.

[0015] The molding and firing process is the same as that of ordinary high-temperature daily-use fine porcelain, and the firing temperature is 1280°C-1350°C.

Embodiment 2

[0016] Example 2 Light yellow ivory yellow body decoration fine porcelain for daily use

[0017] The composition of the carcass porcelain clay is expressed in terms of mass and number: 23 parts of quartz, 12 parts of feldspar, 10 parts of kaolinite powder, 14 parts of washed kaolin, 5 parts of kaolin, 24 parts of kaolinite, 5 parts of clay, and bentonite 2 parts, 5 parts of ivory yellow porcelain body powder, 4 parts of ivory yellow clay, 0.39 parts of vanadium zirconium yellow pigment. The ivory yellow body mud mentioned above is the mud made from the above ingredients except the ivory yellow body mud and the ivory yellow porcelain body powder. Porcelain bodies composed of ingredients other than porcelain body powder are obtained by crushing inferior or waste products of porcelain products obtained after firing.

[0018] The molding and firing process is the same as that of ordinary high-temperature daily-use fine porcelain, and the firing temperature is 1280°C-1350°C.

Embodiment 3

[0019] Example 3 Yellow ivory yellow body decoration fine porcelain for daily use

[0020] The composition of matrix porcelain clay is expressed in terms of mass and number: 22 parts of quartz, 11 parts of feldspar, 9 parts of kaolinite powder, 15 parts of washed kaolin, 6 parts of kaolin, 23 parts of kaolinite, 6 parts of clay, and bentonite 1 part, 6 parts of ivory yellow porcelain body powder, 5 parts of ivory yellow base mud, 0.6 part of vanadium zirconium yellow pigment. The ivory yellow body mud mentioned above is the mud made from the above ingredients except the ivory yellow body mud and the ivory yellow porcelain body powder. Porcelain bodies composed of ingredients other than porcelain body powder are obtained by crushing inferior or waste products of porcelain products obtained after firing.

[0021] The molding and firing process is the same as that of ordinary high-temperature daily-use fine porcelain, and the firing temperature is 1280°C-1350°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention discloses ivory yellow unfired pottery decoration daily service fine ceramics. The unfired pottery components weight parts is that quartz 22-24 parts, feldspar 11-13 parts, kaolinite powder 9-11 parts, desilting kaolin 13-15 parts, kaolin 4-6 parts, kaolinite 23-25 parts, cohesive soil 4-6 parts, bentonite 1-3 parts, ivory yellow porcelain unfired pottery powder 4-6 parts, ivory yellow cog mud 3-5 parts, vanadium zirconium yellow pigment 0.12-0.65 part. It's forming and burning technique is same to normal high temperature fine ceramics, calcining temperature is 1280-1350 degrees C. Pure iron and titanium compound in natural ceramics material can present porcelain capability and yellow color capability in high temperature. This capability is used in this invention, and yellow, pale yellow and faint yellow color can be made by using synthetic dyestuff and its natural characteristic.

Description

technical field [0001] The invention relates to a high-temperature hard porcelain, in particular to an ivory-yellow body-decorated daily-use fine porcelain, which belongs to the technical field of ceramic product production. Background technique [0002] Among the porcelain products, fine porcelain was used for daily use in the past, and the porcelain body was basically white. With the changes of the times, people's aesthetics and consumption concepts are also changing, especially in foreign countries, the colors of daily-use porcelain products are even more diverse, among which, ivory-yellow body-decorated daily-use fine porcelain is the most popular. . my country's porcelain firing industry has a long history and occupies an important position in the world. In the traditional porcelain making process, the yellow porcelain body is made by adding different types and different amounts of yellow agents to the body mud, such as vanadium zirconium yellow material, and the glaz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/16C04B33/13C04B33/14
Inventor 秦继荣靳福顺
Owner 邯郸臣邦陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com