Cationic dyed mixed-fibre processed filament and its production
A production method, cationic technology, applied in the direction of conjugated synthetic polymer artificial filament, etc., can solve the problems of process extension, unsatisfactory, yarn fineness increase, etc., and achieve good dyeing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1:
[0020] 50% by weight of cationic dyeable PET and 50% by weight of ordinary PET are passed through different micropores of the same spinneret during spinning to obtain concentric mixed filaments with the above weight ratio;
[0021] The mixed fiber yarn obtained above is subjected to false twist processing. During false twist processing, the yarn processing speed is 500m / min, the hot needle temperature HP: 80°C, the draft multiple ID before and after the hot needle: 1.45, and the total draft multiple TD: 1.71, Hot plate temperature HT: 200℃. The normal polyester filament part of the obtained product is in the form of coarse and fine details in the length direction.
[0022] The obtained thick and small fancy yarn has a tenacity of 3.73 cN / dtex, an elongation of 14.5%, a CV% of 2.02%, and a U% of 1.84%. After processing, the coarse and detailed fancy yarns are dyed after knitting, the cationic dye is black, and the disperse dye is yellow, and three colors of dark...
Example Embodiment
[0023] Example 2:
[0024] 70% by weight of cationic easy-dyeable PET and 30% by weight of ordinary PET are passed through different micropores of the same spinneret during spinning to obtain the group-type mixed fiber yarn with the above-mentioned weight ratio;
[0025] The mixed fiber yarn obtained above is subjected to false twist processing. During false twist processing, the yarn processing speed is 350m / min, the hot needle temperature HP: 75°C, the draft multiple ID before and after the hot needle: 1.28, and the total draft multiple TD: 1.60, hot plate temperature HT: 180℃. The normal polyester filament part of the obtained product is in the form of coarse and fine details in the length direction.
[0026] The obtained thick and small fancy yarn has a strength of 3.33 cN / dtex, an elongation of 20.2%, a CV% of 2.3%, and a U% of 1.74%. After processing, the coarse and detailed fancy yarns are dyed after knitting, the cationic dye is blue, and the disperse dye is red, and three...
Example Embodiment
[0027] Example 3:
[0028] 30% by weight of cationic dyeable PET and 70% by weight of ordinary PET are passed through different micropores of the same spinneret during spinning to obtain concentric mixed filaments with the above weight ratio;
[0029] The mixed fiber yarn obtained above is subjected to false twist processing with incomplete drafting. During false twist processing, the total draft ratio is 2.4, the hot needle temperature during false twist processing is 45 ℃, and the draft ratio before and after the hot needle is 1.6 , The hot plate temperature is 150℃. The normal polyester filament part of the obtained product is in the form of coarse and fine details in the length direction.
[0030] The obtained thick and small fancy yarn has a tenacity of 2.89 cN / dtex, an elongation of 18.7%, a CV% of 2.2%, and a U% of 1.56%. After processing, the coarse and detailed fancy yarns are dyed after knitting, the cationic dye is blue, and the disperse dye is red, and three colors of ...
PUM
Property | Measurement | Unit |
---|---|---|
Powerful | aaaaa | aaaaa |
Powerful | aaaaa | aaaaa |
Powerful | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap