Method of producing an aluminum alloy brazing sheet

A technology of brazing sheet and manufacturing method, applied in manufacturing tools, chemical instruments and methods, welding medium, etc., can solve problems such as unusability

Inactive Publication Date: 2007-06-20
FURUKAWA SKY ALUMINUM CORP
View PDF7 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the pipe is added with Mg in the sacrificial anode material, it can be used as a raw material for welding flat tubes where the sacrificial anode material is not in cont

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0066] Next, the present invention will be described in more detail based on examples, but the present invention is not limited thereto.

[0067] The core material, the intermediate material and the sacrificial anode material alloy with the metal components and compositions shown in Tables 1, 2, and 3 are respectively cast by mold casting, and after plane cutting is carried out on both sides respectively, finishing machining is carried out. Tables 4 and 5 Homogenization of core material, intermediate material and sacrificial anode material is carried out at the temperatures indicated. 4045 alloy was used as the brazing filler metal, and the brazing filler metal, the intermediate material and the sacrificial anode material were respectively rolled to a thickness of 6 mm by hot rolling. As shown in Tables 4 and 5, these alloy materials are combined on a core material with a thickness of 22mm. At this time, the cladding ratios of the brazing material, intermediate material and sa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

A method of producing an aluminum alloy brazing sheet which has a clad of a sacrificial anode material/a core alloy/an intermediate material/a filler alloy, each of which has a specific composition, wherein number density ratios N 1 /N 2 and N 1 /N 3 each are 1.5 or more, in which a number density ((the number of grains)/[mu]m 3 ) of an intermetallic compound having a sphere-equivalent grain diameter of 0.1 [mu]m or less present in the core alloy, the intermediate material, and the sacrificial anode material, is represented by N 1 , N 2 , and N 3 , respectively.

Description

technical field [0001] The present invention relates to a method for manufacturing an aluminum alloy brazing sheet used in a heat exchanger for automobiles, and in particular, to a method for forming cooling water or refrigerant passages suitable for heat exchangers such as radiators and condensers The manufacturing method of the aluminum alloy brazing sheet used as the material. Background technique [0002] Aluminum alloys are used in automotive heat exchangers such as radiators, condensers, evaporators, heaters, intercoolers, and the like because they are lightweight and have high thermal conductivity. Heat exchangers for automobiles are mainly manufactured by the brazing method. Usually, brazing is performed at a high temperature of about 600° C. using an Al—Si alloy brazing material. Therefore, there is a need for an aluminum alloy brazing sheet that is excellent in brazeability and has high strength and corrosion resistance after brazing. [0003] A heat exchanger m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B15/01B23K35/24C22C21/00C22C21/02C22C21/10C22C21/12F28F21/08
CPCC22C21/10B32B15/016C22C21/14B23K35/286C22C21/02C22C21/00C22C21/08C22C21/16B23K35/28
Inventor 福元敦志新仓昭男
Owner FURUKAWA SKY ALUMINUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap