Manufacturing method of nanometer squama and special equipment thereof

A special equipment and scale technology, which is applied in the field of preparation of nano scale materials or nano scale composite materials, can solve the problems of high cost, low quality and low efficiency, and achieve the effects of performance improvement, good permeability resistance and high corrosion resistance

Inactive Publication Date: 2007-07-04
白日忠
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to solve the problems of high cost, low efficiency, and low quality in powder fine processing, and to combine the usual ultra-fine process steps—crushing, mixing, dispersing, surface treatment, modification, destepping, and nano Simplify the combination of powder synthesis and realize the one-step preparation of nanoscale flake materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of nanometer squama and special equipment thereof
  • Manufacturing method of nanometer squama and special equipment thereof
  • Manufacturing method of nanometer squama and special equipment thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 1

[0032] The working cylinder volume of the planetary ball mill used in this example with both revolution and rotation speed adjustable is 460ml, the processed material is 100 mesh quartz powder, the grinding ball is steel ball, and the dispersant, protective agent and solvent are triethanolamine, six Sodium metaphosphate, ethanol.

[0033] 1. According to the volume of the working cylinder, the weight of the processed material quartz powder is 115g. Weigh 115g of quartz powder and add it into the working cylinder.

[0034]2. According to the volume of the working cylinder, five specifications of bearing steel balls are selected (13 / 16)″; (19 / 32)″; (3 / 8)″; (5 / 16)″; (7 / 32) "."

[0035] The weights of various bearing steel balls are (13 / 16)″358.2g; (19 / 32)″154.7g; (3 / 8)″109.5g; (5 / 16)″10.1g; (7 / 32) "10.6 g.

[0036] 3. Calculate the weight of the dispersant, protective agent and solvent according to the weight of the material as 10 g of triethanolamine; 1 g of sodium hexametap...

preparation Embodiment 2

[0040] The working cylinder volume of the planetary ball mill used in this example, which can be adjusted in revolution and rotation, has a volume of 460ml, the processed material is 200 mesh iron powder, the grinding ball is a steel ball, and the dispersant, protective agent and solvent are respectively triethanolamine; Sodium metaphosphate; water.

[0041] 1. According to the volume of the working cylinder, the weight of iron powder to be processed is 200g. Weigh 200g of iron powder and add it into the working cylinder.

[0042] 2. According to the volume of the working cylinder, five specifications of bearing steel balls are selected (13 / 16)″; (19 / 32)″; (3 / 8)″; (5 / 16)″; (7 / 32) "."

[0043] The weights of various bearing steel balls are (13 / 16)″358.2g; (19 / 32)″154.7g; (3 / 8)″109.5g; (5 / 16)″10.1g; (7 / 32) "10.6 g.

[0044] 3. According to the weight of the material, the weight of the dispersant, protective agent and solvent is calculated as triethanolamine 10g; sodium hexam...

preparation Embodiment 3

[0048] The volume of the planetary ball mill used in this example is 1820ml, the processed material is 320 mesh iron powder, the grinding ball is steel ball, the dispersant and protective agent are respectively epoxy resin; polysulfide Rubber, solvent is xylene, acetone, butanol weight ratio is xylene: acetone: butanol=2:1:2.

[0049] 1. According to the volume of the working cylinder, the weight of titanium powder to be processed is 600g. Weigh 600g of titanium powder and add it into the working cylinder.

[0050] 2. According to the volume of the working cylinder, five specifications of bearing steel balls are selected (13 / 16)″; (19 / 32)″; (3 / 8)″; (5 / 16)″; (7 / 32) "."

[0051] The volumes of various bearing steel balls are (13 / 16)″188.7ml; (19 / 32)″86.2ml; (3 / 8)″55.6ml; (5 / 16)″5.8ml; (7 / 32) "5.4ml.

[0052] 3. According to the weight of the material, the weight of the dispersant, protective agent and solvent is calculated as 42g of epoxy resin; 42g of polysulfide rubber; th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
thicknessaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention belong to the field of superfine powder processing and nano-powder processing, specially it is the preparation methods and equipment for nano-scale materials or nano-scale composite materials, the invention solved the problems of high costs, low efficiency, low quality in powders fine processing. The invention make the usual process of ultrafine steps - crushed, mixed, decentralization, surface treatment, modification, releasing step and nanopowder synthesis simplified merger, make one step produce the nano-scale materials come ture by using proprietary equipment 'planetary ball mill which the revolution and rotation speed can be adjust'. The thickness of Nano-scale is 10 ~ 100 nm, radial size ranged from 0.5 to 50 mu m, is one-dimensional nanomaterials, overcoming the secondary combination step problems in conventional ultrafine powder processing, and easy to spread in different use occasions.

Description

technical field [0001] The invention belongs to the field of powder superfine processing and nanometer powder processing, and specifically relates to a preparation method of nano scale material or nano scale composite material and special equipment thereof. Background technique [0002] With the advancement of science and technology, the development of powder industry has entered the field of nanoscale, which is one of the trends in the development of international powder technology. While the world powder industry is developing towards refinement, the important role of industrial powder deep processing technology in scientific research and industrial production is more and more fully reflected. Countries all over the world start with crushing equipment, and gradually expand to ultra-fine grading, high-uniformity mixing, surface treatment, nano-powder preparation and other aspects. [0003] In recent years, my country's powder industry has also formed a scale along with the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B02C17/08B02C17/24B02C17/18B02C17/20
Inventor 白日忠张巨生程瑾宁
Owner 白日忠