High-wearing high performance-cost ratio flux-cored wire

A flux-cored wire, cost-effective technology, applied in welding media, welding equipment, welding/cutting media/materials, etc., can solve the problems of poor wear resistance of flux-cored welding wire and high price of imported flux-cored welding wire, saving steel and repetitive labor. , It is convenient for large-scale promotion and application, and the effect of good toughness

Inactive Publication Date: 2009-06-10
徐龙江
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the common problems of wear-resistant surfacing flux-cored wires are: low-priced flux-cored wires have poor wear resistance, and the price of imported flux-cored wires with good wear resistance is too high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Drug core formula:

[0017] Powdered graphite 4.5%

[0018] High carbon ferrochrome 65%

[0019] Medium carbon ferromanganese 3.2%

[0020] 45 ferrosilicon 2.5%

[0021] Ferrovanadium 3.5%

[0022] Ferromolybdenum 3%

[0023] Reduction of iron powder balance.

[0024] The filling rate is 45%.

[0025] Manufacturing method: It is manufactured by steel strip method. Cut the steel strip into a certain width steel strip→clean→dry the steel strip→roll the steel strip into a "U"-shaped groove in the forming machine unit→add powder according to the ratio through the powder adding unit→join the edges in the seaming unit →The diameter is reduced to the required diameter by the wire drawing unit →Enter the wire take-up machine →The finished flux-cored wire.

[0026] The average hardness of welding wire surfacing layer is HRC52.

Embodiment 2

[0028] Drug core formula:

[0029] Powdered graphite 6%

[0030] High carbon ferrochrome 70%

[0031] Medium carbon ferromanganese 405%

[0032] 45 ferrosilicon 3%

[0033] Ferrovanadium 2%

[0034] Ferromolybdenum 4%

[0035] Reduction of iron powder balance.

[0036] The fill rate is 60%.

[0037] Manufacturing method is the same as embodiment 1.

[0038] The average hardness of welding wire surfacing layer is HRC59.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flux-cored wire with high abrasion resistance and high performance / cost ratio, an external wrapper of which adopts H08A low carbon steel. The invention is characterized in that: a filling rate of the wire is 30 to 70 percent, percentages by weight of components of the wire and other components are: powdered graphite is 2 to 12 percent, high carbon ferrochromium is 25 to 85 percent, mid-carbon fe-mn is 2 to 15 percent, 45 ferrosilicon alloy is 1 to 7.5 percent, ferrovanadium is 1 to 26 percent, ferromolybdenum is 1 to 10 percent and reduced iron powder accounts for the residual percentage. The beneficial effects of the invention are that: the wire is processed through ordinary metal alloy powder lot, no pure metal or compound is needed, and the cost is relatively lower but the abrasion resistance is relatively higher, thereby being favorable for popularizing and applying widely.

Description

Background technique [0001] Flux cored wire is developed on the basis of tubular electrodes. Because the flux-cored wire has the advantages of stable arc, small spatter, beautiful shape, and the flux core formula can be adjusted according to the mechanical properties of the weld, it can be manufactured in large quantities and used continuously in actual welding. Compared with solid welding wire and manual welding rod, the production efficiency is high, the operating environment of welders is improved, and the comprehensive advantages of flux-cored welding wire are very popular among people. At present, flux cored wire has been widely used in construction, bridge, chemical industry, metallurgy, electric power and other manufacturing and repair industries. [0002] At present, the common problems of wear-resistant surfacing flux-cored wires are: low-priced flux-cored wires have poor wear resistance, and the price of imported flux-cored wires with good wear resistance is too hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/30
Inventor 徐龙江
Owner 徐龙江
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com