Heat unbinding polyurethane finishing agent resistant to crushing, and production method

An anti-wrinkle finishing agent, polyurethane technology, applied in fiber treatment, textiles and papermaking, natural fibers, etc., can solve the problem of poor anti-wrinkle effect

Inactive Publication Date: 2007-07-25
LIAONING FIXED STAR FINE CHEM
View PDF2 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The anti-wrinkle effect of silicone and polyvinyl ac

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1

[0041] Raw materials and ratio (weight):

[0042] a. Hydroxyl-terminated polybutadiene (hydroxyl value 56) 120

[0043] b. Trimethylolpropane 6

[0044] c. Dimethylolpropionic acid 13

[0045] d. IPDI 90

[0046] e. Caprolactam 37

[0047] f. N-Methylpyrrolidone 100

[0048] g. Ammonia (20%) 20

[0049] h. Deionized water 550

[0050] Process method:

[0051] Add a, b, c, d, f into the reaction kettle, react at 70-100°C for 3-7 hours, add e and react at 70-105°C for 4-7 hours, cool down to 30-50°C, and discharge in Stir and emulsify in an emulsification tank with g and h added, and then filter and discharge to obtain the product.

experiment example 2

[0053] Raw materials and ratio (weight):

[0054] a. Hydroxyl-terminated polysiloxane (hydroxyl value 56) 100

[0055] b. Glycerol 5

[0056] c. Dimethylolpropionic acid 10

[0057] d. Hydrogenated MDI 100

[0058] f. Dioxane 80

[0059] e. Acetone oxime 28

[0060] g. Ammonia (20%) 20

[0061] h. Deionized water 478

[0062] Process method: as described in Example 1.

experiment example 3

[0064] Raw materials and ratio (weight):

[0065] a. Hydroxyl-terminated polybutadiene (hydroxyl value 56)

[0066] Or 60 parts of hydroxyl-terminated polysiloxane (hydroxyl value 112)

[0067] b. Trimethylolpropane 6 parts

[0068]c. Dimethylolbutyric acid 15

[0069] d. MDI 115

[0070] e. Phenol 36

[0071] f. Dimethylformamide 100

[0072] g. Ammonia (20%) 24

[0073] h. Deionized water 580

[0074] Process method: as described in Example 1.

[0075] The method of using the thermally unblocked polyurethane anti-wrinkle finishing agent of the present invention: mix this product with water to form an aqueous solution with a content of 3-10%, and after padding the fabric at room temperature, pre-bake it at 80-100°C for 3 minutes, and then dry it at 120-150°C. °C for 3 minutes.

[0076] The test results of the heat-unlocking polyurethane anti-wrinkle finishing agent of the present invention after the anti-wrinkle finishing of cotton fabrics are as follows:

[0077] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a thermal deblocking polyurethane crease-resisting finishing agent. Its composition includes (by wt%) 20-60% of hydroxyl terminated polymer whose average mole mass is 400-6000; 0.1-10% of tribasic alcohol compound; 6-20% of dimethylol carboxylic acid compound; 20-50% of polyisocyanate compound; 6-30% of isocyanate blocking agent and 0.6-6% of ammonia water. Said invention also provides its preparation method and concrete steps.

Description

technical field [0001] The invention relates to a water-based polyurethane resin anti-wrinkle finishing agent for cotton fabrics. [0002] The polyurethane resin anti-wrinkle finishing of the present invention contains 20-60% of polymer weight-terminated polybutadiene; [0003] The anti-wrinkle finish of the polyurethane resin of the invention is a kind of heat-deblocking polyurethane, and the content of the sealing agent is 2-40% of the weight of the polymer. Background technique [0004] At present, most of the non-ironing finishing agents that replace formaldehyde are polycarboxylic acid compounds. For example: "Preparation of Formaldehyde-Free Finishing Agent BTCA" disclosed in "Printing and Dyeing Auxiliaries" magazine 1999 16 (12) 19-21; "Synthesis and Application of Ironing Finishing Agent"; "Printing and Dyeing Auxiliaries" magazine 1998 15 (5) 1-6 disclosed "polyacid a formaldehyde-free non-iron finishing agent published in printing and dyeing auxiliaries"; Europe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/564D06M101/02
Inventor 严欣宁杨文堂仇凯倪成涛
Owner LIAONING FIXED STAR FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap