Surface layer abrasion-proof paper

A wear-resistant paper and surface layer technology, applied in the field of surface wear-resistant paper, can solve the problems of easy delamination between the paper surface and the board, poor waterproof performance, non-wear resistance, etc., and achieve the effect of low cost, complete variety and long service life

Active Publication Date: 2008-03-26
SHANDONG QIFENG SPECIAL PAPER
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Before the product came out, it was initially printed on Polaroid paper, coated with adhesive on the back, and cold pressed onto wood-based panels for finishing. This method pollutes a lot, the paper surface and the board are easy to delaminate, and the waterproof performance is poor. and not wear-resistant
According to the search of "Chinese Patent", there is no surface wear-resistant paper that can match the wood-based panel veneer products, which can improve and improve the wear resistance and stain resistance of the original veneer, and expand the application field of the wood-based panel veneer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] After preparing the materials, calculate by weight: add 98% cellulose pulp mixture (long fiber wood pulp 60%, cellulose pulp 40%), 1% white corundum (Al 2 o 3 ) 1μm composite wear-resistant material. 0.01% additives (PAE wet strength agent 95%, anionic surfactant 0.05%, silicone degassing agent 4.95%), the beating concentration is controlled at 2%, the beating degree is 16°SR, and the pH is adjusted to 5.5-7, as a slurry mixture. Production of surface wear-resistant paper with a grammage of 14 grams.

Embodiment 2

[0020] After preparing the materials, calculate by weight: add 97% cellulose pulp mixture (long fiber wood pulp 80%, cellulose pulp 20%), 2% white corundum (Al 2 o 3 ) 3 μm composite wear-resistant material. 2% additives (PAE wet strength agent 95%, anionic surfactant 0.05%, silicone degassing agent 4.95%), the beating concentration is controlled at 2%, the knocking degree is 16°SR, and the pH is adjusted to 5.5-7, as a slurry mixture. Production of surface wear-resistant paper with a grammage of 18 grams.

Embodiment 3

[0022] After preparing the materials, calculate by weight: add 95% long-fiber wood pulp, add 15% white corundum (Al 2 o 3 ) 60μm compound wear-resistant material, 5% additives (93% PPE wet strength agent, 1% anionic surfactant, 1% binary retention aid, 5% organic silicon degassing agent,), beating concentration control At 2%, the degree of beating is 18°SR, and the pH is adjusted to 5.5-7 with a chelating agent, as a slurry mixture. Production of surface wear-resistant paper with a grammage of 22 grams.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The surface wear resistant paper for making decorating thermosetting laminated sheet contains stuffing and assistant. It has high transparency, high wear resistance, long service life, environment friendship and other advantages. It is applied widely for the surface of furniture, vehicle, ship, airplane, floor, instrument, etc.

Description

technical field [0001] Surface layer wear-resistant paper, the invention relates to a surface layer wear-resistant paper directly used for manufacturing thermosetting decorative laminates. Background technique [0002] Before the product came out, it was initially printed on Polaroid paper, coated with adhesive on the back, and cold pressed onto wood-based panels for finishing. This method pollutes a lot, the paper surface and the board are easy to delaminate, and the waterproof performance is poor. And not wear-resistant. According to the search of "Chinese Patent", there is no surface wear-resistant paper that can match the wood-based panel veneer products, which can improve and improve the wear resistance and stain resistance of the original veneer, and expand the application field of the wood-based panel veneer. . Contents of the invention [0003] The technical problem to be solved by the present invention is to fill up the gap in the prior art and provide a surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H27/28D21H17/67
Inventor 李学峰
Owner SHANDONG QIFENG SPECIAL PAPER
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com