Wear-resistant alloy cast iron modified material and method for manufacturing grinding plate blank casting thereby

A technology of modified materials and wear-resistant alloys, which is applied in the field of spherical material manufacturing, can solve the problems of low grinding efficiency and short service life, and achieve the effects of easy operation, high mechanical strength and impact toughness, and excellent wear resistance

Inactive Publication Date: 2008-05-14
施伟晶 +1
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of low grinding efficiency and short service life of existing grinding plates, and provide a wear-resistant alloy cast iron modified material and a method for manufacturing grinding plate blank castings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant alloy cast iron modified material and method for manufacturing grinding plate blank casting thereby

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0012] Specific embodiment 1: In this embodiment, the wear-resistant alloy cast iron modified material is made of alloy cast iron and nano-rare earth modified material, and the nano-rare earth modified material accounts for 0.01-5.00% of the total weight of the wear-resistant alloy cast iron modified material. The alloy cast iron is Cr-Mo-Cu alloy cast iron, W-Cr-Cu alloy cast iron, W-Cr-Cu-Mn alloy cast iron, Cr-Mo-Cu-Ni alloy cast iron, Mo-Ni alloy cast iron, gray cast iron , White cast iron or ductile iron. The nano-rare earth modified material is a rare earth element and / or a rare earth compound with a particle size of 1 to 500 nm.

[0013] When the rare earth modified materials in this embodiment are a mixture, various rare earth modified materials can be mixed in any ratio.

specific Embodiment approach 2

[0014] Specific embodiment two: this embodiment is different from specific embodiment one in that the nano-rare earth modified material accounts for 0.02-2.00% of the total weight of the wear-resistant alloy cast iron modified material. Others are the same as the first embodiment.

specific Embodiment approach 3

[0015] Specific embodiment three: This embodiment is different from specific embodiment one in that the nano-rare earth modified material accounts for 0.1% of the total weight of the wear-resistant alloy cast iron modified material. Others are the same as the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a wear resistant alloy cast iron modified material and a method thereof of fabricating nog plate blank casting, pertaining to a sphere material fabrication technology. The problems of low grinding processing efficiency and short service life of present nog plate are solved. Wear resistant alloy cast iron materials are fabricated by cast iron and nano rare earth modified material. The nano rare earth modified material accounts for 0.01 to 5.00 percent of total weight of wear resistant alloy cast iron modified materials; alloy cast iron comprises Cr-Mo-Cu alloy cast iron, W-Cr-Cu alloy cast iron, W-Cr-Cu-Mn alloy cast iron, Cr-Mo-Cu-Ni alloy cast iron, Mo-Ni alloy cast iron, gray cast iron, white cast iron or ductile cast iron; the grain diameter of the nano rare earth modified material is 1 to 500nm of lanthanon and / or rare earth compounds; the nog plate blank casting fabricating method employs a melting casting method. The grinding processing efficiency of the nog plate fabricated by the wear resistant alloy cast iron modified material of the invention is higher than existing nog plate by more than 50 percent and the service life is twice or more as that of the existing nog plate and the application range is wide. The fabrication technic of the invention is characterized by simple technique and easy operation.

Description

Technical field [0001] The invention belongs to the manufacturing technology of spherical materials; in particular, it relates to a grinding plate modified material and a grinding plate blank for grinding and grinding spherical materials such as steel balls, tungsten alloy balls, ceramic balls, glass balls, agate balls and other handicraft balls. Method of casting manufacturing. Background technique [0002] The high-tech machinery industry needs high-precision, high-quality bearings and steel balls. In recent years, my country’s steel ball industry has made rapid progress and has become a world steel ball producer, but not a strong country. The main reason is that the steel balls produced in my country have high precision and quality. Less than the level of the world's strong steel ball production country. Therefore, improving the surface accuracy of steel balls in our country, producing high-quality steel balls, and building a world powerhouse of steel balls, is placed in front...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C37/06
Inventor 王铀姜国林施伟晶
Owner 施伟晶
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com