Ground fabric for masking for use in method of transfer piece dyeing of embroidered part
A post-dyeing and embroidery cloth technology, applied in dyeing method, transfer printing method, embroidery machine mechanism, etc., can solve problems such as difficulty, increase of process, pre-removal of masking material process, cost control and other problems
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0061] As the water-soluble fiber, use the PVA fiber that is made by the PVA of degree of polymerization 1750, degree of saponification 88 mol%, monofilament fineness 2.2dtex, the crimped PVA fiber of intensity 5.0cN / dtex, make the PVA fiber that is formed by 100 mass parts Weight per unit area 60.8g / m 2 Random mesh (non-woven fabric). Overlaid on the non-woven fabric is made of PVA with a degree of polymerization of 1750 and a degree of saponification of 88 mol%, with a strength of 8 N / cm and a weight per unit area of 25 g / m 2 The PVA film is thermally fused between a heated embossing roll and a steel roll to produce a base cloth for masking. The embossing conditions were 12% bonding area ratio, 160° C. temperature, 40 kgf / cm linear pressure, and 10 m / min processing speed.
[0062] After covering this base fabric for masking on the base fabric for embroidery and performing embroidery, the embroidered part is dyed using transfer paper. During transfer dyeing, bleeding or ...
Embodiment 2
[0064] As the water-soluble fiber, use the PVA fiber that is made by the PVA of degree of polymerization 1750, degree of saponification 96 mol%, monofilament fineness 1.7dtex, the crimped PVA fiber of strength 5.5cN / dtex, make the PVA fiber that is formed by 100 mass parts Weight per unit area 49.6g / m 2 Random mesh (non-woven fabric). Overlaid on the non-woven fabric is made of PVA with a degree of polymerization of 1750 and a degree of saponification of 96 mol%, with a strength of 8 N / cm and a weight per unit area of 25 g / m 2 The PVA film is thermally fused between a heated embossing roll and a steel roll to produce a base cloth for masking. The embossing conditions were 12% of bonded area ratio, 180°C temperature, 40 kgf / cm linear pressure, and 10 m / min processing speed.
[0065] After covering this masking base fabric on the embroidery base fabric and performing embroidery, the embroidered part is dyed using transfer paper. During transfer dyeing, bleeding or migration...
Embodiment 3
[0067] 90 mass parts of PVA short fibers with a monofilament fineness of 1.7dtex and a fiber length of 3mm made of PVA with a degree of polymerization of 1750 and a saponification degree of 96 mol%, and binder fibers (vinylon) with a monofilament fineness of 1.1dtex and a fiber length of 3mm Binder) 10 parts by mass were dispersed in water to prepare a slurry. Using this slurry, a 2-layer bonded wet paper was obtained using a short-wire-cylinder paper machine, and dried using a Yankee dryer to obtain a weight per unit area of 41.6 g / m 2 , 2-layer paper with a melting temperature of 70°C in water. Overlay on this water-soluble paper is made of PVA with a degree of polymerization of 1750 and a degree of saponification of 96 mol%, with a strength of 8 N / cm and a weight per unit area of 25 g / m 2 The PVA film is thermally fused between a heated embossing roll and a steel roll to produce a base cloth for masking. The embossing conditions were 12% of bonded area ratio, 180°C te...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
| strength | aaaaa | aaaaa |
| strength | aaaaa | aaaaa |