Increment method for extracting natural environmental protection adhesive from machilus pauhoi

A natural environmental protection and adhesive technology, applied in natural resin adhesives, adhesive types, adhesives, etc., can solve the problems of reducing the utilization value of nanmu, high processing power consumption cost, and large waste of rubber materials. To achieve the effect of value-added utilization, low cost, and little waste of rubber loss

Inactive Publication Date: 2008-07-02
张先和
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the direct use of pulverized slippery nanmu wood as the adhesive material (commonly known as incense powder) of the mosquito-repellent incense matrix, the loss and waste of the rubber material is large during the crushing process, and the processing power consumption cost is high, especially when using the wood powder containing its unique colloid. While being used as a mosquito-repellent-repellent incense base binder, it brings smoke pollution due to the burning of mosquito-repellent incense and burns a large amount of usable wood, which greatly reduces the utilization value of nanmu.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Use Phoebe (commonly known as incense powder wood) wood as raw material to extract natural environmental protection adhesive suitable for the manufacture of environmentally friendly smokeless mosquito coils:

[0014] ① Slicing and grinding the slippery nanmu wood;

[0015] ②Put the smooth nanmu wood that has been treated in ① into the container, add normal temperature water (the water does not drop the wood at least) and soak for 6-8 hours.

[0016] ③Put the smooth nanmu wood treated (soaked) in ② together with its soaking liquid into a container with 60 mesh holes and squeeze it until the liquid dries out after fully stirring, and then filter the squeezed liquid to obtain the natural environmental protection sticky nanmu wood. Mixture, this natural environment-friendly adhesive can be used to manufacture environment-friendly smokeless mosquito-repellent incense (replacing the original wood incense powder or chemical adhesive), and the separated wood can be used as pape...

Embodiment 2

[0018] Use Phoebe (commonly known as incense powder wood) wood as raw material to extract natural environmental protection adhesive suitable for the manufacture of environmentally friendly smokeless mosquito coils:

[0019] ① Slicing and hot-grinding the smooth nanmu wood;

[0020] ② Put the smooth nanmu wood processed in ① into the container, add normal temperature water (at least the water does not drop the wood) and soak for 5-10 hours.

[0021] ③Put the smooth nanmu wood treated (soaked) in ② together with its soaking liquid into a container with 60 mesh holes and squeeze it until the liquid dries out after fully stirring, and then filter the squeezed liquid to obtain the natural environmental protection sticky nanmu wood. Mixture, this natural environment-friendly adhesive can be used to manufacture environment-friendly smokeless mosquito-repellent incense (replacing the original wood fragrance powder or chemical adhesive), and the separated slippery nanmu wood is used as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for extracting a natural environment-friendly adhesive from phoebe nanmu wood and for achieving increment of phoebe nanmu. In order to overcomes the disadvantages of the prior art, which directly adopts pulverized phoebe nanmu wood material as an adhesive material for a mosquito coil base, such as smoke pollution caused by burning the mosquito coil and burn-up of large amount of useful wood materials, the invention subjects the phoebe nanmu wood material to the treatment for increasing the surface area, water addition treatment, separation of phoebe nanmu wood material, and extraction of natural environment-friendly adhesive. The invention is used for processing and treatment of phoebe nanmu wood, and the extracted natural environment-friendly adhesive can be used as the adhesive material for a mosquito coil base to substitute for the prior pulverized phoebe nanmu wood material and can be used for manufacturing environment-friendly smokeless mosquito coil. The rest of the phoebe nanmu wood material can be used as the raw materials of paper, synthetic fiberboard, etc, thus achieving increment of phoebe nanmu.

Description

technical field [0001] The invention relates to a wood utilization method, that is, a value-added method for extracting natural environmental protection adhesives from nanmu. Background technique [0002] The existing utilization of sliding nanmu (being commonly called as incense powder firewood) mainly is that sliding nanmu timber is pulverized, as the gluing raw material (being commonly called as incense powder) of mosquito-repellent incense matrix. Due to the direct use of pulverized slippery nanmu wood as the adhesive material (commonly known as incense powder) of the mosquito-repellent incense matrix, the loss and waste of the rubber material is large during the crushing process, and the processing power consumption cost is high, especially when using the wood powder containing its unique colloid. While being used as the mosquito-repellent incense base binder, it brings smoke pollution and burning a large amount of available wood due to the burning of mosquito-repellent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine