Degumming liquid

A technology of glue and high molecular polymer, which is applied in the field of chemical treatment liquid, can solve the problems of increased grinding processing burden, long time, surface corrosion of metal parts, etc., and achieve high degumming efficiency, low degumming temperature and short degumming time Effect

Inactive Publication Date: 2008-07-30
SHENYANG POLYTECHNIC UNIV
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is difficult to separate the parts after cutting. It takes a long time to separate the parts by vibration, and the solid film remaining on the surface of the parts has a great influence on the phosphating or electroplating of the parts.
Degumming is carried out by boiling water, and the surface of metal parts is seriously corroded, which increases the burden of subsequent grinding processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Dichloroethane 40 kg

[0015] Acetone 40 kg

[0016] White oil 10 kg

[0017] Paraffin 1 kg

[0018] High molecular polymer 0.1 kg

[0019] Co-solvent for high molecular polymer 8.9 kg

[0020] The use temperature is 20-30°C.

Embodiment 2

[0022] Dichloromethane 40 kg

[0023] Acetone 40 kg

[0024] White oil 10 kg

[0025] Paraffin 1 kg

[0026] High molecular polymer 0.1 kg

[0027] Co-solvent for high molecular polymer 8.9 kg

[0028] The use temperature is 20-30°C.

Embodiment 3

[0030] Dichloromethane 50 kg

[0031] Acetone 40 kg

[0032] White oil 5 kg

[0033] Paraffin 0.5 kg

[0034] High molecular polymer 0.05 kg

[0035] 4.45 kg of co-solvent for high molecular polymer

[0036] The use temperature is 30-40°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a degumming solution and belongs to a chemical treatment solution, which is used for removing a fastening glue film adhering to the surface of mechanical parts. The invention provides a degumming solution that has a short degumming duration and has no corrosion to the mechanical parts. The invention consists of halogenated hydrocarbon, acetone, paraffin, white oil, a high molecular polymer and the latent solvent for the high molecular polymer. The degumming solution is characterized in that the weight percentage for the components is as follows: halogenated hydrocarbon 30 to 50 percent, white oil 4 to 10 percent, acetone 40 to 60 percent, high molecular polymer 0.05 to 0.1 percent, paraffin 0.5 to 2 percent and the rest is the latent solvent for the high molecular polymer.

Description

Technical field: [0001] The invention belongs to chemical treatment liquid and is mainly used for removing the fixed adhesive film adhered to the surface of mechanical parts. Background technique: [0002] At present, chemical adhesives are widely used in the processing of small mechanical parts. In order to improve production efficiency, some mechanical processing enterprises first bond small raw materials together with adhesives, and then cut them. It is difficult to separate the parts after cutting. It takes a long time to separate the parts by vibration, and the solid film remaining on the surface of the parts has a great influence on the phosphating or electroplating of the parts. Degumming is carried out by boiling with water, and the surface of metal parts is seriously corroded, which increases the burden of subsequent grinding. Invention content: [0003] The present invention aims at the above problems and provides a degumming solution with short degumming time a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G5/02
Inventor 娄桂艳赵清梁吉艳
Owner SHENYANG POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products