Composition for making flower bowl and flower stand as well as method thereof

A composition and technology for flower pot stand, which are applied in the directions of botanical equipment and methods, manufacturing tools, gardening, etc., can solve problems such as high cost and energy waste, and achieve the effects of good air permeability, energy saving and low cost

Inactive Publication Date: 2008-08-27
王玉金
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The task of the present invention is to provide a composition for making flowerpots and flower stands that utilizes low-cost materials and solves the problems of energy waste and high cost through non-burning.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Take 300Kg of silica sand powder and 700Kg of cement, mix the two materials evenly, stir them with water to form a viscous shape, and then put the viscous mixture into a mold of a predetermined shape and size, and make the mold sticky The mixture is pressed for 30 hours at a temperature of 30°C to be molded, and then the molded part is taken out of the mold and placed in a room temperature environment for the first drying. The drying time is 15 hours, and then the molded part is placed Soak in water for 50 hours, take it out of the water and then dry it for a second time at 40°C, and dry it for the second time until the moisture in the molded part is completely volatilized, and the molded part obtained is the finished flower pot or flower stand.

Embodiment 2

[0019] Take 800Kg of silica sand powder and 200Kg of cement, make molded parts according to the method of Example 1, and perform the first drying and second drying. When making the molded parts, let the viscous mixture in the mold be at a temperature of 40℃ Press down for 20 hours to make it into a shape. The first drying time is 10 hours. After soaking in water for 40 hours, the second drying is performed. The drying temperature is 30°C. The flowerpot is obtained when the moisture in the molded part is completely volatilized. Or the flower stand is the finished product.

Embodiment 3

[0021] Take 700Kg of silica sand powder and 300Kg of cement, make molded parts according to the method of Example 1, and perform the first drying and second drying. When making molded parts, let the viscous mixture in the mold be at a temperature of 35℃ Press down for 24 hours to make it into shape. The first drying time is 12 hours. After soaking in water for 43 hours, the second drying is carried out. The drying temperature is 35℃. The flowerpot is obtained when the moisture in the molded part is completely volatilized. Or the flower stand is the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a composition for fabricating flowerpots and flower stands, which comprises silica flour and cement, wherein the percentage by weight is 30%-80% of silica flour and 20%-70% of cement. The flowerpots and flower stands fabricated by employing the composition are low in cost and harmless to plants, further as the mode of baking-free is employed to produce the flowerpots and flower stands by the composition, not only the energy can be saved, but also the flowerpots can be produced with the shape similar to the shape of plants root, namely root carving, thereby sound decorating action of the flowerpot can be achieved, further more, the two inorganic substances of silica and cement are harmless to plants and have excellent air permeability.

Description

Technical field: [0001] The invention relates to a composition for making flower pots and flower stands, and a method for making flower pots and flower stands by using the composition. Background technique: [0002] Flower pots are parts used for cultivating flowers, and flower stands are shelves specially used to place potted flowers. Flower pots and flower stands are usually placed in rooms or guest houses. Therefore, flower pots and flower stands are required to have a good decorative effect, and their appearance and shape are particularly important. The flower pots in the prior art are made of ceramics or purple sand materials. Among them, ceramics are made of inorganic metal minerals such as clay or aluminosilicate minerals or certain oxides as the main raw materials, and are mixed, shaped and calcined. It is made into flower pots and other products; while purple sand is a kind of iron-containing clay siltstone. When making flower pots, it also needs to be mixed, formed and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B14/06B28B3/00A01G9/02
CPCC04B2111/802C04B41/5022C04B41/009C04B28/04C04B2111/00267
Inventor 王玉金
Owner 王玉金